Abstract:<p>A circumferential crack in the fusion line is a major threat to the structural integrity of the pipeline girth weld because it may possibly lead to fracture failure when subjected to large plastic deformations. For the newly constructed X80 pipeline with an outside diameter (OD) of 1422 mm in China, the complicated configuration of welded joints and the outer diameter are outside the range of the general fracture assessment standards, such as BS 7910. Furthermore, during the pipe manufacture process, pipeline designers merely specify the minimum yield strength limit according to the pipe steel grade. This results in a wide variation range in the choice of yield strength values of the base metal. This also leads to a serious problem in the fracture assessment of pipe girth weld because the weld strength is commonly considered to be either evenly matched or overmatched. The foregoing factors make it difficult to perform an accurate fracture assessment using conventional standards. This study therefore aims to investigate the fracture behavior of 1422-mm OD pipelines with a double-V groove weld and circumferential crack in the fusion line. The specific effect of material mismatch and the realistic operational parameters that influence the fracture capacity of the pipe are examined via a series of numerical investigations. First, a rigorous three-dimensional finite element model to simulate the pipe girth weld is established by utilizing the ABAQUS finite element code package. The weld, which has a canoe-shaped surface crack in the fusion line between the heat-affected zone and root welding metal, is subjected to biaxial loading conditions. The keyhole method is adopted to simulate the crack front as well as the crack tip to eliminate the stress singularity effect during deformation. A refined mesh strategy is introduced to ensure the accurate simulation of the stress and strain fields in the vicinity of the crack tip. Based on the numerical model, the J-integral fracture parameter, which is clearly defined based on a strict mechanical theory, is chosen to characterize the effect of strength matching ratio, internal pressure, and yield to tensile strength ratio on the crack driving force. A new strain-based J-integral prediction formula is proposed based on numerical results.</p>

Flow-Accelerated Corrosion Damage in a Steam Pipe Girth Weld

Effect of Fusion Boundary Microstructure on Flow-Accelerated Corrosion Cracking

Characterization of Flow-Accelerated-corrosion of Pressure Piping Welded Joints

Flow enhanced corrosion of tee in gas transmission pipeline

Inhomogeneous Strain Behaviors of the High Strength Pipeline Girth Weld under Longitudinal Loading

Failure analysis of corrosion at an inhomogeneous welded joint in a natural gas gathering pipeline considering the combined action of multiple factors

Finite element analysis of the failure of high-strength steel pipelines containing group corrosion defects

Microstructural Understanding of Flow Accelerated Corrosion of SA106B Carbon Steel in High-Temperature Water with Different Flow Velocities

Flow-Induced Corrosion Simulation on a Plate by Finite Element Methods

Corrosion Failure Analyses of an Elbow and an Elbow-to-pipe Weld in a Natural Gas Gathering Pipeline

The Effect of Pipeline Root Weld Microstructure on Crack Growth Behaviour

Influence of Internal Corrosive Defect on the Burn-Through of In-Service Welding on Pipelines

Environmentally Assisted Cracking of Forged 316LN Stainless Steel and Its Weld in High Temperature Water

Three-dimensional Finite Element Analysis of Residual Stresses in Circumferential Welds of 2205/X65 Bimetallic Pipe

Thermal corrosion fatigue crack growth behavior and life prediction of 304SS pipeline structures in high temperature pressurized water

Fracture response of 1422-mm diameter pipe with double-V groove weld joints and circumferential crack in fusion line

Failure Analysis of Girth Weld Cracking in Gas Transmission Pipelines Subjected to Ground Subsidence and Traffic Loads

The Effect of Flowing Velocity and Impact Angle on the Fluid-Accelerated Corrosion of X65 Pipeline Steel in a Wet Gas Environment Containing CO2

Investigation of the tensile strain response of the girth weld of high-strength steel pipeline

Role of welding residual stress in stainless steel piping with application of the leak-before-break technology

Effects of fluid dynamics Parameters on flow-accelerated corrosion at elbow of carbon steel pipeline