Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Corrosion behaviour of X80 pipeline steel welded joint in H2O- saturated supercritical-CO2 environment

Corrosion behavior of X70 steel in the supercritical CO2 mixed with SO2 and saturated water

Investigation of Supercritical CO2 Corrosion Behavior of X80 Carbon Steel in Pipelines: an in Situ Experimental and DFT Study

Corrosion Behavior of Pipeline Steel Welds in Simulated Produced Water with Different Co2 Partial Pressures under High Temperature

CO2 corrosion behavior of simulated heat-affected zones for X80 pipeline steel

Long term corrosion of X70 steel and iron in humid supercritical CO 2 with SO2 and O2 impurities

CO2 Corrosion of X80 Steel under High Shear Flow Fields

Corrosion Behavior and Mechanism of X80 Pipeline Steel Welded Joints under High Shear Flow Fields

Effect Of Temperature On Corrosion Behaviour Of X70 Steel In High Pressure Co2/So2/O-2/H2o Environments

Long term corrosion of X70 steel and iron in humid supercritical CO2with SO2and O2impurities

Corrosion behavior of the weld joint of X80 pipeline steel in an acidic red soil

Corrosion Behavior of Reheated CGHAZ of X80 Pipeline Steel in H2S-containing Environments

Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions

Corrosion characteristics of simulated reheated heat-affected-zone of X80 pipeline steel in carbonate/bicarbonate solution

Corrosion Behavior of X80 Pipeline Steel and Its Weld Joint in Ku'erle Soil Environment

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

CO 2 corrosion behavoir of X70 pipeline steel

Corrosion Behaviors of X80 Pipeline Steel in Different Simulated Alkaline Soil Solution

Corrosion Behavior of X80 Steel Welded Joint in Simulated Natural Gas Condensate Solutions

Study on corrosion properties of pipelines in simulated produced water saturated with supercritical CO2

Corrosion Behavior and In-Situ Ph Monitoring of a 3% Chromium Low Alloy Pipeline Steel Welded Joint in a CO2 Environment