Abstract:SiC layer was prepared in an industrial scale spout fluidized bed by chemical vapor deposition. The density of SiC coating was about 3.18 g/cm(3). High temperature oxidation experiments were carried out at different temperatures from 800 to 1600 degrees C. The microstructure and composition were characterized using different methods, including mass change weighing, XRD, EDS and SEM. It was found that the weight gain of SiC coating layer was not obvious below 1200 degrees C, and subsequent mass gain gradually increased with increasing temperature, reaching 10% at 1600 degrees C. High-magnification SEM results show that the oxidation began from the surface and gradually formed punctate distribution of the oxide. Small crystal structure (similar to micron) of the SiC surface was very clear at 1000 degrees C, and this crystal structure disappeared gradually at high temperatures, forming oxides of Si in the SiC surface. There was a stacking fault stress due to the different thermal expansion coefficients and elastic modulus of SiC and Si oxides, leading to the gradual formation of cracks around the punctates. With increasing temperature, the crack further increased the oxidation rate of SiC, and finally the formed Si oxides layer fell off from the particles. It can be seen clearly that the layer was peeling when the temperature was increased to 1400 degrees C. Increasing the temperature to 1600 degrees C, the SiC coating was oxidized completely into a honeycomb structure, with obvious sintering of SiC. XRD analysis shows that there was a growing SiO2 peaks from 1400 degrees C, indicating that surface oxidation was significant. EDS results shows that the oxygen content in the coating surface gradually increased with increasing temperature. Semi-quantitative analysis shows that the surface was close to SiO2 at 1600 degrees C.

Study on the High Speed Chemical Vapor Deposition for SiC Coating

Low temperature synthesis and formation mechanism of dense SiC coating layer by fluidized bed chemical vapor deposition

Studies of synthesizing the SiC nanometer powders by chemical vapor reaction

Thermodynamic Analysis of Chemical Vapor Deposition Process for SiC/SiO2 Graded Composite Coating

High-throughput thermodynamic analysis of the CVD of SiC from the SiCl4-CH4-H2 system

SiC Interlayer/diamond Coatings Prepared on Cemented Carbide Micro-Tools by High Current DC Extended Arc Chemical Vapor Deposition

Atomistic Insights into Chemical Vapor Deposition Process of Preparing Silicon Carbide Materials Using ReaxFF-MD Simulation

Preparation, Performance and Nuclear Applications of Silicon Carbide Materials Prepared by FB-CVD Method

Characteristics of ZrC Barrier Coating on SiC-Coated Carbon/Carbon Composite Developed by Thermal Spray Process

Study of GeSi Alloy Deposition on Ge Substrate by Very Low-Pressure Chemical Vapor Deposition

Ablation mechanism and morphology evolution of the HfC-SiC coating for C/C composites deposited by supersonic atmospheric plasma spraying

High Temperature Oxidation Behavior of SiC Coating Materials

Self-densification behavior, interfacial bonding and cyclic ablation resistance of HfSi2-ZrSi2 modified SiC/ZrB2-SiC/SiC coating for Cf/SiC composite

Characterization of Silicon Carbide Films Prepared by Chemical Vapor Deposition

Preparation and Characterization of SiC Layer of Coated Fuel Particles for High-Temperature Gas-Cooled Reactor

Effects of SiC on microstructure and properties of plasma sprayed ZrB2–ZrC composite coating

Effect of C/Si Ratio on the Characteristics of 3C-Sic Films Deposited on Si(100) Base on the Four-Step Non-Cooling Process

Preparation of Silicon Carbide Nanowires and Nanochains Using Chemical Vapor Deposition Method

Preparation of Silicon Carbide Coating Layer by Fluidized Bed Chemical Vapor Deposition Using a Halogen-Free Precursor

SiC Coating on HTR Graphite Spheres Prepared by Fluidized-Bed Chemical Vapor Deposition

Cathode plasma electrolytic deposition of Al2O3 coatings doped with SiC particles