Abstract:SiC layer was prepared in an industrial scale spout fluidized bed by chemical vapor deposition. The density of SiC coating was about 3.18 g/cm(3). High temperature oxidation experiments were carried out at different temperatures from 800 to 1600 degrees C. The microstructure and composition were characterized using different methods, including mass change weighing, XRD, EDS and SEM. It was found that the weight gain of SiC coating layer was not obvious below 1200 degrees C, and subsequent mass gain gradually increased with increasing temperature, reaching 10% at 1600 degrees C. High-magnification SEM results show that the oxidation began from the surface and gradually formed punctate distribution of the oxide. Small crystal structure (similar to micron) of the SiC surface was very clear at 1000 degrees C, and this crystal structure disappeared gradually at high temperatures, forming oxides of Si in the SiC surface. There was a stacking fault stress due to the different thermal expansion coefficients and elastic modulus of SiC and Si oxides, leading to the gradual formation of cracks around the punctates. With increasing temperature, the crack further increased the oxidation rate of SiC, and finally the formed Si oxides layer fell off from the particles. It can be seen clearly that the layer was peeling when the temperature was increased to 1400 degrees C. Increasing the temperature to 1600 degrees C, the SiC coating was oxidized completely into a honeycomb structure, with obvious sintering of SiC. XRD analysis shows that there was a growing SiO2 peaks from 1400 degrees C, indicating that surface oxidation was significant. EDS results shows that the oxygen content in the coating surface gradually increased with increasing temperature. Semi-quantitative analysis shows that the surface was close to SiO2 at 1600 degrees C.

Preparation and Characterization of SiC Layer of Coated Fuel Particles for High-Temperature Gas-Cooled Reactor

Design and preparation of SiC based novel coated fuel particle

Properties of SiC Coated Layer for HTGR Fuel Particles

Study of SiC layer with fine grains in HTGR coated fuel particles

Structure of Sic Coatings from Polycarbosilane on Graphite for Fuel Element Matrix of High Temperature Gas-Cooled Reactor

Preparation and Performance of Fully Ceramic Fuel Element Using Silicon Carbide As Coating Layers

SiC Coating on HTR Graphite Spheres Prepared by Fluidized-Bed Chemical Vapor Deposition

Preparation, Performance and Nuclear Applications of Silicon Carbide Materials Prepared by FB-CVD Method

Preparation of ZrC Layer of Coated Fuel Particle for High-Temperature Gas-Cooled Reactor by Chemical Vapor Deposition with ZrCl4 Vapor

Oxidation mechanism of SiC coated layer in air atmosphere at 1400°C

Preparation of Silicon Carbide Coating Layer by Fluidized Bed Chemical Vapor Deposition Using a Halogen-Free Precursor

SiC Performance of Coated Fuel Particles under High-Temperature Atmosphere of Air

Dual layer SiC coating on matrix graphite sphere prepared by pack cementation and fluidized-bed chemical vapor deposition

Corrosion of SiC layers on coated zirconia particles in wet atmosphere

SiC Coatings Fabricated by Chemical Vapor Reaction on Graphite

SiC/SiO2 oxidation-resistant coatings on fuel element matrix graphite of high temperature gas-cooled reactor

Low temperature synthesis and formation mechanism of dense SiC coating layer by fluidized bed chemical vapor deposition

Preparation and Characterization of Zirconium Carbide Coating on Coated Fuel Particles

The Research Progress of Zrc Coating Layer of Fuel Particles for Htgr at Home and Abroad

Micro Four‐Layer SiC Coating on Matrix Graphite Spheres of HTR Fuel Elements by Two‐Step Pack Cementation

High Temperature Oxidation Behavior of SiC Coating Materials