Abstract:In order to improve the oxidation and ablative properties of C/C composites, ZrB2-SiC-HfB2-TaSi2 coating was prepared on the surface of C/C composites by atmospheric plasma spraying. By means of microstructure analysis and phase structure analysis, the difference of the spray powder before and after IPS treatment and the microstructure and oxidation ablation resistance of the coating were studied. The results show that the IPS treated powder has better fluidity and densification. In the coating, part of ZrB2 and HfB2 exist in the form of unmelted particles, another part exists in the form of intermediate solid solution (Zr, Hf)B2, and TaSi2 exists in the particle gap. The linear ablation rate and mass ablation rate of the coating are −1.513 × 10−4 mm/s and 2.842 × 10−4 g/s, respectively, measured under the condition of oxygen acetylene heat flux of 1.8 MW/m2, 180 s were ablated. The coating has good ablative resistance, and TaSi2 can form dense Zr-Ta-O and Hf-Ta-O oxides with Zr and Hf elements. The Ta-Si-O glass phase can effectively seal the holes of the coating to prevent oxygen penetration. During the ablation process, the oxidation of (Zr,Hf)B2 also plays a certain role in the formation of densification zone on the coating surface.

Ablation mechanism and morphology evolution of the HfC-SiC coating for C/C composites deposited by supersonic atmospheric plasma spraying

Oxidation ablation resistance of ZrB2-HfB2-SiC-TaSi2 coating prepared on C/C composite surface

Mechanical properties and ablation resistance of La2O3-modified HfC-SiC coating for SiC-coated C/C composites

WSi2 modified HfB2-SiC coating: Microstructure and ablation resistance

Influences of deposition temperature, gas flow rate and ZrC content on the microstructure and anti-ablation performance of CVD-HfC-ZrC coating

Microstructure and ablation behavior of C/C–HfC–SiC composites fabricated by reactive melt infiltration with Hf–Si alloy

Ablation behavior of high-entropy boride (Hf-Zr-Ta-Ti)B 2 coating fabricated via supersonic atmospheric plasma spraying for carbon/carbon composites

MoSi2-HfC/TaC-HfC multi-phase coatings synthesized by supersonic atmospheric plasma spraying for C/C composites against ablation

High-quality SiC-HfC coating with interpenetrating structure based on a two-step low temperature molten salt method

Cyclic ablation behavior and microstructure evolution of multi-layer coating on C/C composites under oxyacetylene torch

Microstructures and ablation resistance of WSi2/ZrSi2/ZrxHf1-xC/SiC coating based on a pattern strengthening one-step method

UHTC coating reinforced by HfC nanowires against ablation for C/C composites

Self-densification behavior, interfacial bonding and cyclic ablation resistance of HfSi2-ZrSi2 modified SiC/ZrB2-SiC/SiC coating for Cf/SiC composite

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Investigation on the oxidation and ablation behaviors of HfB2-SiC-Si/SiC-Si coatings for carbon/carbon composites

Microstructure and Ablation Behavior of W/ZrC/SiC Coating on C/C Composites Prepared by Reactive Melt Infiltration and Atmospheric Plasma Spraying

Anti-ablation Performance of Plasma Sprayed ZrB2/SiC Coatings on C/C Substrates and the Influence of a Chemical Vapor Deposited SiC Interlayer

Effect of tantalum carbide on the ablation behaviors of hafnium carbide coating for C/C composites under single and cyclic oxyacetylene torch environments

Phase and microstructure evolutions of in-situ ZrC composite coating under plasma torch ablation

Effect of Si, Al2O3 additives on the ablation behavior of ZrB2-SiC coating with Al2O3-modified SiC bond coat for C/C composites

TaSi2 modified HfB2‐SiC coating: preparation and ablation behavior