Abstract:In order to improve the oxidation resistance of carbon fibers reinforced carbon matrix composites (C/C) and the thermal shock resistance of ultra-high temperature ceramics (UHTCs), large numbers of ZrB2 based particles were introduced into C/C composites to fabricate the C/C-UHTC composites by powder infiltration (PI) and isothermal chemical vapor infiltration (ICVI). The effects of UHTC additive, heat flux and ablation time on the ablation behaviors of the C/C-UHTC composites were investigated through exposure to an oxyacetylene torch flame with ultra-high temperature. The ZrB2 addition to the C/C pronouncedly improved the ablation resistance of the material under a 3920kW/m2 heat flux and the C/C–ZrB2 showed a better ablation-resistive property compared to the C/C–4ZrB2–1SiC, C/C–2ZrB2–1SiC, C/C–2ZrB2–1SiC–1HfC and C/C–2ZrB2–1SiC–1TaC. With decrease of the heat flux from 3200 to 2380kW/m2, the presence of a small amount of SiC in the C/C–ZrB2 was found to have a positive role of improving the ablation resistance; the C/C–4ZrB2–1SiC exhibited a good ablation-resistive endurance under 2380kW/m2. The HfC addition was proved to effectively enhance the ablation property of the C/C–1ZrB2–2SiC while the TaC addition severely deteriorated the property.

UHTC coating reinforced by HfC nanowires against ablation for C/C composites

SiC Nanowires Toughed HfC Ablative Coating for C/C Composites

Effects of HfC/PyC Core-Shell Structure Nanowires on the Microstructure and Mechanical Properties of Hf1-xZrxC Coating

Microstructure and ablation performance of HfC/PyC core-shell structure nanowire-reinforced Hf1-xZrxC coating

Ablation Resistance of ZrC-based Composite Coating with Multi-Layer Structure for Carbon/carbon Composites above 2200 °C

Preparation and ablation resistance of ZrC nanowires-reinforced CVD-ZrC coating on sharp leading edge C/C composites

Influences of deposition temperature, gas flow rate and ZrC content on the microstructure and anti-ablation performance of CVD-HfC-ZrC coating

Effect of tantalum carbide on the ablation behaviors of hafnium carbide coating for C/C composites under single and cyclic oxyacetylene torch environments

Preparation and long-term ablation behavior of Cf-reinforced ZrC-SiC coated C/C-ZrC-SiC composite

Ablation mechanism and morphology evolution of the HfC-SiC coating for C/C composites deposited by supersonic atmospheric plasma spraying

Ablation behaviors of ultra-high temperature ceramic composites

Ablation behavior of HfC coating with different thickness for carbon/carbon composites at ultra-high temperature

Fabrication and ablation property of carbon/carbon composites with novel SiC–ZrB2 coating

Effect of SiCnws@BN core shell upon impact-ablation performance of HfC coating on C/C composites

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Ablation behavior of high-entropy boride (Hf-Zr-Ta-Ti)B 2 coating fabricated via supersonic atmospheric plasma spraying for carbon/carbon composites

Microstructures and ablation resistance of WSi2/ZrSi2/ZrxHf1-xC/SiC coating based on a pattern strengthening one-step method

WSi2 modified HfB2-SiC coating: Microstructure and ablation resistance

Effect of HfC addition on ablation behavior of SiBCN ceramics

A novel Hf0.75Zr0.25N solid solution coating with high mechanical strength: Ablation protection application above 2200°C

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration