Abstract:C/C-ZrC-SiC composites were produced by the joint processes of chemical liquid-vapor deposition (CLVD) and precursor infiltration and pyrolysis (PIP), and the effects of deposition period in CLVD process on the preparation, microstructure and anti-ablation property were studied. The results displayed the non-woven layers of the composites was preferred to be densified in CLVD method, but the subsequent PIP process could fill the pores of the fiber webs. Thus the joint technologies reduced the porosity of the composites and improved the content of ceramics. Meanwhile, the insufficient deposition in CLVD process led to large amounts of defects, which were not densified fully in the following PIP. However, the excessive deposition of CLVD filled the pores remarkably, so the channels for precursor infiltration in the subsequent PIP were reduced. When the deposition period was 8 h, the sample C8P9 had a low porosity, high ceramics content and uniform distribution, which was responsible for its outstanding ablation resistance. After ablation for 60 s, sample C8P9 was damaged slightly, and its mass and linear ablation rate was 1.22 x 10(-3) g/s and 1.07 x 10(-3) mm/s. The ablation surface was divided into four regions, and the different oxide coatings were generated on these regions. These coatings could provide effective protection for the composites, which made a significant contribution to improve the ablation resistance.

Preparation and long-term ablation behavior of Cf-reinforced ZrC-SiC coated C/C-ZrC-SiC composite

Ablation Behaviors and Mechanism of ZrC-SiC-Si/SiC-Si Double-Layered Coatings on C/C Composite under Plasma Flame at 3000 °C

A ZrCSiC/SiC multilayer anti-ablation coating for ZrC modified C/C composites

Ablation Resistance of ZrC-based Composite Coating with Multi-Layer Structure for Carbon/carbon Composites above 2200 °C

Ablation behavior of C/C-ZrC-SiC composite with gradient distribution of ZrC-SiC ceramics along the thickness

Ablation Behavior of the ZrC Coating on C/C Composite with the Construction of Thermal Dispersal Network

Ablation Behavior of ZrC–SiC Coated C/C–ZrC–SiC Composites Prepared by Precursor Infiltration Pyrolysis Combined with Reactive Melt Infiltration

Microstructure and Ablation Property of C/C-ZrC-SiC Composites Fabricated by Chemical Liquid-Vapor Deposition Combined with Precursor Infiltration and Pyrolysis

Preparation and Ablation Behavior of a ZrB2-SiC Coating-Matrix Integrated C/C Composite

Ablation Resistance of SiC–ZrC Coating Prepared by a Simple Two-Step Method on Carbon Fiber Reinforced Composites

Ablation Behaviors of SiC Nanowire-Reinforced ZrC-SiC Coating-Matrix Integrated C/C Composites with Different Ratios of Precursors

Preparation and ablation properties of ZrC-SiC coating for carbon/carbon composites by solid phase infiltration

Enhanced Anti-Ablation Performance of Carbon/carbon Composites Modified with ZrC-SiC

One-step Preparation and Ablation Behavior of ZrC-SiC-Si Coating for Nose-Shaped ZrC/C Composites with Gradient Pore Structure by Vapor Silicon Infiltration

Ablation Resistance and Mechanism of SiC/ZrC-ZrB2double Layer Coating for C/C Composites under Plasma Flame

SiC/ZrB2–SiC–ZrC Multilayer Coating for Carbon/carbon Composites Against Ablation

A Multilayer SiC/ZrB2/SiC Ablation Resistance Coating for Carbon/Carbon Composites

ZrB2-SiC coating to protect carbon/carbon composites against ablation

Ablation resistance and mechanism of SiC/ZrC-ZrB2 double layer coating for C/C composites under plasma flame

Anti-ablation performance of plasma sprayed ZrB 2 /SiC coatings on C/C substrates and the influence of a chemical vapor deposited SiC interlayer

Ablation Behavior of (zrc/sic)3 Alternate Coating Prepared on Sharp Leading Edge C/C Composites by CVD