Abstract:The oxide layer formed by ultra‐high melt point oxides (ZrO2, HfO2) and SiO2 glassy melt is the key to the application of traditional thermal structural materials in extremely high‐temperature environment. However, the negative effect of ZrO2 and HfO2 phase transitions on the stability of oxide layer and rapid volatilization of low viscosity SiO2 melt limit its application in aerospace. In this study, the ablation behavior of Cf/(CrZrHfNbTa)C‒SiC high‐entropy composite was explored systematically via an air plasma ablation test, under a heat flux of 5 MW/m2 at temperatures up to 2450°C. The composite presents an outstanding ablation resistance, with linear and mass ablation rates of 0.9 μm/s and 1.82 mg/s, respectively. This impressive ablation resistance is attributed to the highly stable oxide protective layer formed in situ on the ablation surface, which comprises a solid skeleton of (Zr, Hf)6(Nb, Ta)2O17 combined with spherical particles and SiO2 glassy melt. The irregular particles provide a solid skeleton in the oxides protective layer, which increased stability of the oxide layer. Moreover, the spherical particles have a crystal structure similar to that of Ta2O5 and are uniformly distributed in SiO2 glassy melt, which hinder the flow of SiO2 glassy melt and enhance its viscosity to a certain degree. And it reduces the volatilization of SiO2. In summary, the stable oxide layer was formed by irregular particles oxide and the SiO2 glassy melt with certain viscosity, thereby resulting in the impressive ablation resistance of the composite. This study fills a gap in ablation research on the (CrZrHfNbTa)C system.

A novel Hf0.75Zr0.25N solid solution coating with high mechanical strength: Ablation protection application above 2200°C

A novel (Hf1/3Zr1/3Ti1/3)C medium-entropy carbide coating with excellent long-life ablation resistance applied above 2100 °C

Ablation behavior of high-entropy boride (Hf-Zr-Ta-Ti)B 2 coating fabricated via supersonic atmospheric plasma spraying for carbon/carbon composites

Cyclic ablation resistance at 2300 °C of (Hf0.4Zr0.4Ta0.2)B2-SiC-Si coating for C/SiC composites prepared by SiC-assisted reactive infiltration of silicon

Ultra-high temperature ablation behavior of CVD-Hf 5 TaC 6 solid solution ceramic coating for C/C composites: Experiment and first-principle calculation

Ablation behavior and mechanisms of Cf/(CrZrHfNbTa)C‒SiC high‐entropy composite at temperatures up to 2450°C

UHTC coating reinforced by HfC nanowires against ablation for C/C composites

Ablation behavior of HfC coating with different thickness for carbon/carbon composites at ultra-high temperature

Nanosized Hf6Ta2O17 particles reinforced HfC ceramic coating for high temperature applications

Novel nitrogen-doped hafnium carbides for advanced ablation resistance up to 3273 K

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Influences of deposition temperature, gas flow rate and ZrC content on the microstructure and anti-ablation performance of CVD-HfC-ZrC coating

Ablation behavior and mechanisms of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high-entropy ceramic matrix composites

Enhanced ablation resistance of ZrC–ZrO2 nanocomposite ceramic coating on TiAlNb medium-entropy alloy prepared by a novel strategy

Engineering Cf /ZrB2 -SiC-Y2 O3 for Thermal Structures of Hypersonic Vehicles with Excellent Long-Term Ultrahigh Temperature Ablation Resistance

Fabrication of low-density carbon-bonded carbon fiber composites with an Hf-based coating for high temperature applications

Ablation Behavior and Mechanism of Double-Layer ZrB2-based Ceramic Coating for Lightweight Carbon-Bonded Carbon Fiber Composites under Oxyacetylene Flame at Elevate Temperature

Multi-cycle and long-term ablation behavior of Cf/ZrB2-SiC composites at 2500 °C

Ablation mechanism of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C-SiC composite during plasma ablation above 2000 °C

Using in-situ conversed nano SiC to bond UHTC particles and construct anti-ablation coating

High heat flux ablation behaviors of Ir-Hf coatings in wind tunnel tests up to 6.6 MW/m2