Abstract:The current generation of ultrahigh temperature ceramic precursors typically encounters obstacles in achieving high ceramic yields ( < 40 wt.%) due to the challenges in integrating significant amounts of boron, which hampers their conversion into boride-based ultrahigh temperature ceramics. To tackle these challenges, a serious of pioneering liquid multi-component hafnium-containing ceramic SiHfCB precursors (with different Hf/Si ratios) have been developed. These novel precursors are featured with stable molecular structure and high ceramic yield which were successfully created through a novel one-pot polymerization process. They present in liquid form and their structure is characterized by C-C bonds forming its main chain with branched chains of O-Si-O, Si-O-Hf, Si-O-B, and B-O-Hf which have untapped advantages including uniform component dispersion, and excellent fluidity. The ceramic yield of SiHfCB precursor with Hf/Si of 0.2 is remarkably up to 68.6 wt.% at 1500 degrees C, and their Hf content exceeded 50 wt.%. Of particular interest, the pyrolyzed product HfB2 -SiC nanopowders derived from the SiHfCB precursor with Hf/Si of 0.2, consist of nanopowders in the 40-60 nm range with a density of 5.23 g cm(-4). Remarkably, this material demonstrates exceptional performance in ultrahigh temperature oxygen-containing environments at 2500 degrees C, showing near-zero ablation with a linear ablation rate of just 2.5 x 10(-4) mm s(-1) . Post-ablation analysis of the microstructure reveals that the formation of a lava-like HfO2 and HfO2 -SiO2 oxide layer effectively blocks oxygen penetration and provides excellent oxidation resistance. The innovative SiHfCB hafnium-containing ceramic precursor offers a groundbreaking solution for the preparation of lightweight ultrahigh-temperature ceramics. This development is poised to provide robust technical support for the use of ultrahigh temperature ceramics in non-ablative thermal protective systems, particularly in the construction of hypersonic vehicles, where ultrahigh temperature resilience is crucial. (c) 2024 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.

Novel nitrogen-doped hafnium carbides for advanced ablation resistance up to 3273 K

Novel refractory high-entropy ceramics: Transition metal carbonitrides with superior ablation resistance

A novel Hf0.75Zr0.25N solid solution coating with high mechanical strength: Ablation protection application above 2200°C

Thermoablative behaviors of designable hafnium carbonitride integrated with lattice of tungsten upon 3273K

Oxidation/ablation behaviors of hafnium carbide-silicon carbonitride systems at 1500 and 2500 C

Microstructure and High-Temperature Ablation Behaviour of Hafnium-Doped Tungsten-Yttrium Alloys

A novel (Hf1/3Zr1/3Ti1/3)C medium-entropy carbide coating with excellent long-life ablation resistance applied above 2100 °C

Ablation behavior and mechanisms of Cf/(CrZrHfNbTa)C‒SiC high‐entropy composite at temperatures up to 2450°C

Ablation behavior of high-entropy carbides ceramics (Hf0.2Zr0.2Ta0.2Nb0.2Ti0.2)C upon exposition to an oxyacetylene torch at 2000 °C

Oxyacetylene ablation of (Hf0.2Ti0.2Zr0.2Ta0.2Nb0.2)C at 1350 − 2050 °C

Ultra-high temperature resistance of one-dimensional hafnium carbide wrapped with pyrolytic carbon up to 2450 °C

Effect of HfC addition on ablation behavior of SiBCN ceramics

Ablation mechanism of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C-SiC composite during plasma ablation above 2000 °C

Ablation behavior of HfC coating with different thickness for carbon/carbon composites at ultra-high temperature

Ultrahigh Temperature Ablation Resistant HfB2-SiC Composites: from Liquid SiHfCB Precursor Synthesis to Light Weight Bulk Preparation and Characterization

Fabrication and Evaluation on Thermal Stability of Hafnium Diboride Matrix Composite at Severe Oxidation Condition

Ablation behavior and mechanisms of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C–SiC high-entropy ceramic matrix composites

Insights into the Bond Behavior and Mechanical Properties of Hafnium Carbide under High Pressure and High Temperature

Enhanced ablation resistance of HfB2-HfC/SiBCN ceramics under an oxyacetylene torch environment

Nanosized Hf6Ta2O17 particles reinforced HfC ceramic coating for high temperature applications

Ablation Behavior of an Ir-Hf Coating: A Novel Idea for Ultra-High Temperature Coatings in Non-Equilibrium Conditions