Abstract:Despite significant efforts to develop ultra-high temperature ceramics, the phase stability together with high hardness and oxidation resistance remains to be addressed in ZrB2-SiC based ceramics. ZrB2-20 vol% SiC (ZS20) ceramics with varying amounts of Si3N4 (2.5, 5 and 10 vol%) were processed by multi stage Spark Plasma Sintering (SPS) over a range of temperature (1800–1900 °C) for 3 min under 50 MPa. All the ZS20-Si3N4 composites could be densified to more than 98% theoretical density (ρth) after SPS at 1900 °C. The XRD, SEM-EDS analysis of the ZS20-Si3N4 composites revealed the presence of reaction product phases (ZrO2, BN, ZrN) along with SiC and ZrB2 major phases. Sintering reactions were proposed to explain the existence of such new phases and extinction of Si3N4. Thermo-Calc software was also used to further confirm the formation of these new phases in the ZS20-Si3N4 samples. The hardness of ZS20-Si3N4 composites varied between 25.50 and 30.56 GPa, in particular, ZrB2-20 vol% SiC-5vol% Si3N4 measured with the maximum hardness. In fact, it is the highest ever reported hardness for the ZrB2 composites. Considering oxidation resistance, the weight gain of ZrB2-20 vol%SiC composites decreased (from 13.84 to 9.84 mg/cm2) and oxide layer thickness increased (64–128 μm) after oxidation at 1500 °C for 10 h in air. The cross sectional microstructure of oxidized ZS20-Si3N4 composites consists of thick dense outer layer of SiO2, intermediate (ZrO2-SiO2) layer and unreacted bulk. The formation of dense SiO2 layer and absence of SiC depleted layer from the oxidized samples are signatures of improved oxidation resistance of Si3N4 reinforced ZrB2-20 vol% SiC.

Microstructure and Thermal Shock Resistance of Zr7/8Ti1/8B2-20 Vol% SiC Composites Synthesized by Mechanical Alloying and Spark Plasma Sintering

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Microstructure, Mechanical Properties and Thermal Shock Resistance of ZrB 2 -Sic-c F Composite with Inhibited Degradation of Carbon Fibers

Microstructures and Mechanical Properties of ZrB2–SiC–Ni Ceramic Composites Prepared by Spark Plasma Sintering

Novel Ti3SiC2-(Ti, Zr)B2 Toughened (ti, Zr)C-based Composites with Enhanced Mechanical Properties Fabricated by Dual in Situ Reactions Hot-Pressing at Low Temperature

Effect of SiC Content on Mechanical Properties and Thermal Shock Resistance of BN–ZrO2–SiC Composites

Improved toughness of ZrB2–SiC composites with nanopowders obtained by mechanical alloying

Microstructure and thermal shock behavior of ZrB2–SiC–graphite composite

The Thermal Shock Resistance Of Zrb2-Sic Ultra-High Temperature Ceramics

Microstructural feature and thermal shock behavior of hot-pressed ZrB2–SiC–ZrO2 composite

Study on the toughening mechanism of in-situ synthesis (TixZr1−x)B2 in solid-state sintered SiC composite ceramics

Enhanced Strengths and Thermal Shock Resistance of SiC-BN-10 Vol% Cf Composites Through ZrB2 Addition

Electrostatic Assembly Preparation of High-Toughness Zirconium Diboride-Based Ceramic Composites with Enhanced Thermal Shock Resistance Performance

Microstructure and high temperature mechanical properties of hot-pressed ZrB2-based composites

Effect of graphite flake on microstructure as well as mechanical properties and thermal shock resistance of ZrB2–SiC matrix ultrahigh temperature ceramics

Toughened (ti0.2zr0.2hf0.2nb0.2ta 0.2)B2-Sic Composites Fabricated by One-Step Reactive Sintering with a Unique SiB6 Additive

Microstructure and mechanical properties of SiC composite ceramics modified by (TixZr1–x)B2 solid solution

Single-cycle thermal shock resistance of ZrB2–SiCnp ceramic composites

Mechanical properties and thermal shock behavior of hot-pressed ZrB2–SiC–AlN composites

Microstructure and mechanical behaviour of transient liquid phase spark plasma sintered B4C–SiC–TiB2 composites from a B4C–TiSi2 system

Phase stability, hardness and oxidation behaviour of spark plasma sintered ZrB2-SiC-Si3N4 composites