Abstract:ZrB2-20 vol.% SiC-10 vol.% h-BN (particles) ceramic composites (ZSB) were fabricated by hot pressing under inert gas protected. ZSB samples with mean size 75 × 55 × 40 mm(3) were heated using current heating method and then cooled down to low temperature by circulating water. ZSB samples repeatedly went through thermal shock with 10-50 times under various conditions, respectively. Diverse effects on residual strength of ZSB at different experiment conditions (temperatures, thermal shock times, and heating rates) were investigated. The test results indicated that the residual strength of specimen materials all reached the maximum while the temperature was 1600 °C and thermal shock number was less than 50 times. Because ZSB samples could not stand the extremely serious hyperoxidation at very high temperature (1800 °C), the residual strength of samples decreased sharply. At 1600 °C, when the thermal shock times was 20, ZSB samples' residual strength reached the maximum, but it decreased to the lowest point while the thermal shock times was 30. So we argued that the sensitive thermal shock number was 30. Finally, we analyzed the influences on samples residual strength generated by different heating rates at the same temperature and thermal shock number; the results showed that when heating rate was equal to cooling rate, the residual strength of specimen materials reached the maximum.

Single-cycle thermal shock resistance of ZrB2–SiCnp ceramic composites

Thermal Shock Property of ZrB_2-Based Ultra-High Temperature Ceramics

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Effect of repeated thermal shock on mechanical properties of ZrB2-SiC-BN ceramic composites

Thermal Shock Behavior of Porous ZrB2–SiC Ceramics

Effect of SiC Content on Mechanical Properties and Thermal Shock Resistance of BN–ZrO2–SiC Composites

Mechanical properties and thermal shock behavior of hot-pressed ZrB2–SiC–AlN composites

Thermal shock behavior of ZrB2–SiC ultra-high temperature ceramics with addition of zirconia

Microstructural feature and thermal shock behavior of hot-pressed ZrB2–SiC–ZrO2 composite

Microstructure and Thermal Shock Resistance of Zr7/8Ti1/8B2-20 Vol% SiC Composites Synthesized by Mechanical Alloying and Spark Plasma Sintering

Enhanced Strengths and Thermal Shock Resistance of SiC-BN-10 Vol% Cf Composites Through ZrB2 Addition

Mechanical Properties of NanoSiC Reinforced ZrB<sub>2</sub>-Based Ceramic Composite

Mechanical Properties of NanoSiC Reinforced ZrB<sub>2</sub>-Based Ceramic Composite

Influence of SiCnp Content on the Microstructure and Mechanical Properties of ZrB2–SiC Nanocomposite

Mechanical Properties of NanoSiC Reinforced ZrB2-Based Ceramic Composite

Thermal shock resistance of ZrC matrix ceramics

Microstructure and thermal shock behavior of ZrB2–SiC–graphite composite

Microstructures and Mechanical Properties of ZrB2–SiC–Ni Ceramic Composites Prepared by Spark Plasma Sintering

Enhanced Mechanical Properties, Thermal Shock Resistance and Ablation Resistance of Si2BC3N Ceramics with Nano ZrB2 Addition

High-Performance Zrb2-Sic-C-F Composite Prepared by Low-Temperature Hot Pressing Using Nanosized Zrb2 Powder

Microstructure, Mechanical Properties and Thermal Shock Resistance of ZrB 2 -Sic-c F Composite with Inhibited Degradation of Carbon Fibers

Single-cycle thermal shock resistance of ZrB2–SiCnp ceramic composites

Thermal Shock Property of ZrB_2-Based Ultra-High Temperature Ceramics

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Effect of repeated thermal shock on mechanical properties of ZrB2-SiC-BN ceramic composites

Thermal Shock Behavior of Porous ZrB2–SiC Ceramics

Effect of SiC Content on Mechanical Properties and Thermal Shock Resistance of BN–ZrO2–SiC Composites

Mechanical properties and thermal shock behavior of hot-pressed ZrB2–SiC–AlN composites

Thermal shock behavior of ZrB2–SiC ultra-high temperature ceramics with addition of zirconia

Microstructural feature and thermal shock behavior of hot-pressed ZrB2–SiC–ZrO2 composite

Microstructure and Thermal Shock Resistance of Zr7/8Ti1/8B2-20 Vol% SiC Composites Synthesized by Mechanical Alloying and Spark Plasma Sintering

Enhanced Strengths and Thermal Shock Resistance of SiC-BN-10 Vol% Cf Composites Through ZrB2 Addition

Mechanical Properties of NanoSiC Reinforced ZrB&lt;sub&gt;2&lt;/sub&gt;-Based Ceramic Composite

Mechanical Properties of NanoSiC Reinforced ZrB<sub>2</sub>-Based Ceramic Composite

Influence of SiCnp Content on the Microstructure and Mechanical Properties of ZrB2–SiC Nanocomposite

Mechanical Properties of NanoSiC Reinforced ZrB2-Based Ceramic Composite

Thermal shock resistance of ZrC matrix ceramics

Microstructure and thermal shock behavior of ZrB2–SiC–graphite composite

Microstructures and Mechanical Properties of ZrB2–SiC–Ni Ceramic Composites Prepared by Spark Plasma Sintering

Enhanced Mechanical Properties, Thermal Shock Resistance and Ablation Resistance of Si2BC3N Ceramics with Nano ZrB2 Addition

High-Performance Zrb2-Sic-C-F Composite Prepared by Low-Temperature Hot Pressing Using Nanosized Zrb2 Powder

Microstructure, Mechanical Properties and Thermal Shock Resistance of ZrB 2 -Sic-c F Composite with Inhibited Degradation of Carbon Fibers

Mechanical Properties of NanoSiC Reinforced ZrB<sub>2</sub>-Based Ceramic Composite