Abstract:Zirconia‐toughened alumina (ZTA) ceramics with high mechanical properties were sintered by hot‐pressing method using SiC particles (SiCp) and SiC whiskers (SiCw) as the reinforcing agents simultaneously. The influences of sintering temperature, SiCp and SiCw contents on the microstructure and mechanical properties of ZTA ceramics were investigated. It was found that both SiCp and SiCw could contribute to grain refinement significantly and promote the mechanical properties of the ceramics. However, the excess addition of SiCp or SiCw led to the formation of pores with large sizes and degraded the mechanical properties instead. When 13 wt% SiCp was introduced, the maximum flexural strength of 1180.0 MPa and fracture toughness of 15.9 MPa·m1/2 were obtained, whereas the maximum flexural strength of 1314.0 MPa and fracture toughness of 14.7 MPa·m1/2 were achieved at 20 wt% SiCw. Interestingly, the simultaneous addition of SiCp and SiCw could further improve the mechanical properties, and the highest flexural strength of 1334.0 MPa and fracture toughness of 16.0 MPa·m1/2 were achieved at a SiCw/SiCp ratio of 16/4. The reinforcement mechanisms in the ceramics mainly included the phase transformation toughening of ZrO2, the crack deflection and bridging of SiCp and SiCw and the pull‐out of SiCw.

Microstructure and mechanical properties of SiC composite ceramics modified by (TixZr1–x)B2 solid solution

Study on the toughening mechanism of in-situ synthesis (TixZr1−x)B2 in solid-state sintered SiC composite ceramics

Effects of SiC Platelet and ZrSi2 Additive on Sintering and Mechanical Properties of ZrB2-based Ceramics by Hot-Pressing

Effects of ZrB2 powders on microstructure and mechanical properties of ZrB2-SiCw ceramics

Microstructures and mechanical properties of reactive spark plasma-sintered ZrB2–SiC–MoSi2 composites

The Fabrication and Mechanical Properties of SiC/ZrB2 Laminated Ceramic Composite Prepared by Spark Plasma Sintering

Microstructures and mechanical properties of TiB2 composite ceramics with co-addition of Ti and TiC fabricated by SPS

Preparation of TiB2–SiC composites toughened with interlocking microstructure by self-assembled TiB2 plates

Preparation And Mechanical Properties Of Zirconium Diboride Matrix Composites Reinforced By Silicon Carbon Platelets

Microstructure evolution, enhanced hardness and toughness in the solid-solution ceramic composite by reaction pressureless sintering of ZrB2 and TiC powders

Processing and Mechanical Properties of Zirconium Diboride‐Based Ceramics Prepared by Spark Plasma Sintering

Preparation, mechanical properties, and toughening mechanisms of SiCw/SiCp‐reinforced zirconia‐toughened alumina ceramics

Effect of temperature on the structure and mechanical properties of SiC–TiB2 composite ceramics by solid-phase spark plasma sintering

Novel (Zr, Ti)B2-(Zr, Ti)C-SiC ceramics via reactive hot pressing

Microstructure, mechanical properties and thermal shock behavior of h-BN-SiC ceramic composites prepared by spark plasma sintering

Effect of Nano SiC on Microstructure and Mechanical Properties of BN-ZrO2-SiC Multiphase Ceramics

Processing, microstructure, and mechanical properties of chopped SiC fibers reinforced ZrB2–hBN–based composites

Correlation between phase content and mechanical properties of SiCw- ZTA composites sintered by SPS

Preparation and Mechanical Properties of Laminated Zirconium Diboride/molybdenum Composites Sintered by Spark Plasma Sintering

Microstructure And Mechanical Properties Of Zrb2-Based Composites With Laminated Structure