Preparation And Mechanical Properties Of Zirconium Diboride Matrix Composites Reinforced By Silicon Carbon Platelets
Wang Mingfu,Wang Chang'An,Yu Lei,Zhang Xinghong
DOI: https://doi.org/10.3321/j.issn:1002-185X.2009.z2.243
2009-01-01
Rare Metal Materials and Engineering
Abstract:The preparation and mechanical properties of zirconium diboride matrix composites reinforced by silicon carbon platelets (SiCpl/ZrB2 composites) have been investigated using 3vol% AlN as sintering additive. Bending strength, fracture toughness, density and Vickers hardness were tested, respectively. Electron Scanning Microscope was used to observe the surface and the ruptured cross section. The additions of Sic platelets were 5 vol%, 10 vol%, 15 vol% and 20 vol%, respectively. The results showed that an adequate addition of SiC platelets could promote the sintering densification of the SiCpl/ZrB2 composites. The mechanical properties of the SiCpl/ZrB2 composites are higher than those of the monolithic ZrB2 ceramic. Bending strength and Vickers hardness of the SiCpl/ZrB2 Composites reached maximum values, (625.34 +/- 21.46) MPa and (14.60 +/- 0.84) GPa, respectively, at an addition of SiC platelets of 5 vol%, while fracture toughness of the SiCpl/ZrB2 Composites reached a maximum value of (8.35 +/- 0.26) MPa.m(1/2) at an addition of Sic platelets of 15 vol%. According to the observation on fractograph of the SiCpl/ZrB2 composites, crack deflection and platelet pulling-out were thought as main toughening mechanisms.