Abstract:ZrB2-20vol% SiC-30vol% Zr–Al–C (ZSA) composite ceramics were fabricated by using graphite powders, SiC powders and ball milled Zr/Al/ZrB2 composite powders through spark plasma sintering. The ball milling process resulted in forming Zr/Al coating layer covered ZrB2 powders and introducing O into the composite powders despite of Ar protective atmosphere. The Zr/Al coating layer reacted with graphite powders to in situ form layered Zr–Al–C grains in ZSA composite ceramics during the sintering process. As increasing milling time longer than 1h, the great increase in the introduced O included by Zr/Al/ZrB2 composite powders leaded to an insufficiency in Al due to the formation of Al2O3, which resulted in a remarkable phase transition from Zr2Al4C5 to Zr3Al4C6 in the ZSA composite ceramics. The more sufficient mixing and combination of Zr, Al and ZrB2 achieved by increasing milling time leaded to the more uniform distribution and the longer slenderness ratio of Zr–Al–C grains in the ZSA composite ceramics, which made the major contribution to the toughening of ZSA composite ceramics. The optimal milling time for Zr/Al/ZrB2 composite powders was 4h and the corresponding ZSA composite ceramic showed the maximum value of fracture toughness, 5.96±0.41MPam1/2, which is about 15% higher than that of the ZSA ceramic sintered using un-milled powders. The longer milling time of 6h leaded to much more Al2O3 and few layered Zr–Al–C grains in the ZSA ceramic that exhibited the minimum fracture toughness. The fracture mode is a mixture of inter- and intra-granular fractures, and the toughening mechanisms are the crack deflection and crack bridging that result from the existed Zr–Al–C grains with laminated microstructure.

Toughness Mechanism of Layered ZrB2 Based Composite Ceramic

Microstructure And Mechanical Properties Of Zrb2-Based Composites With Laminated Structure

Strong and Tough ZrB2 Materials Using a Heterogeneous Ceramic-Metal Layered Architecture

Preparation And Mechanical Properties Of Zrb2-Based Laminated Composites

Laminated ZrB2–SiC Ceramic with Improved Strength and Toughness

Microstructure and Mechanical Properties of Laminated ZrB2–SiC Ceramics with ZrO2 Interface Layers

The Fabrication and Mechanical Properties of SiC/ZrB2 Laminated Ceramic Composite Prepared by Spark Plasma Sintering

Laminated ZrB2–SiC/graphite Ceramics with Simultaneously Improved Flexural Strength and Fracture Toughness

Toughening of Laminated ZrB2–SiC Ceramics with Residual Surface Compression

Mechanical Properties of Short Carbon Fiber Reinforced ZrB2–SiC Ceramic Matrix Composites

Preparation and Mechanical Properties of Laminated Zirconium Diboride/molybdenum Composites Sintered by Spark Plasma Sintering

Bioinspired Tough and Strong ZrB2-SiCw/Ti–Nb–Ti Hybrid Composites with a Hierarchical Ceramic-Metal Architecture

Toughening Effect of Short Carbon Fibers in the ZrB2–ZrSi2 Ceramic Composites

Effect of ball milled Zr/Al/ZrB2 composite powders on microstructure and toughening of ZrB2–SiC/Zr–Al–C composite ceramics sintered by spark plasma sintering

Effects of SiC Platelet and ZrSi2 Additive on Sintering and Mechanical Properties of ZrB2-based Ceramics by Hot-Pressing

Influence of the Microstructure Evolution of ZrO2 Fiber on the Fracture Toughness of ZrB2–SiC Nanocomposite Ceramics

Microstructure and Mechanical Properties of ZrB2–Nb Composite

The Fabrication and Mechanical Properties of Bionic Laminated ZrB2–SiC/BN Ceramic Prepared by Tape Casting and Hot Pressing

Microstructure and mechanical properties of ZrB2–SiC–ZrO2f ceramic

Microstructure and Mechanical Properties of ZrB2-SiC Composites

Microstructure and mechanical properties of ZrB2–SiC nanocomposite ceramic