Abstract:In the present work, effects of ZrC addition (10, 15, 20, 25 vol%) on microstructure and mechanical properties of ZTA20mol% (Zirconia-20mol% Toughened Alumina) ceramic composites were investigated. Samples were prepared by Hot Pressing Sintering (HP) at 1 600 ℃ and 30 MPa for a soaking time of 2 hours. Microstructures were characterized by XRD, Raman, SEM and TEM. XRD and Raman spectra results revealed that only ZrC, α-Al2O3 and ZrO2 were detected for all composites, indicating that these ceramic composites had excellent chemical compatibilities. SEM images showed refined microstructure was obtained, and the fracture surfaces exhibited a mixed process of transgranular and intergranular fracture. According to the TEM observations, some nano-sized ZrC particles dispersed inside Al2O3 grains and formed an intra/inter-type nanostructure. The relative densities and Vickers hardness were inversely proportional to ZrC content, which gradually decreased from 98.24% to 94.89%, from 1 847 to 1 691 HV1, respectively. Flexural strength and fracture toughness were tested by three-point bending method and single-edge notched beam method, respectively. The fracture toughness increased at first and then decreased with ZrC content increased from 0 to 25 vol%. The maximum value was 11.23 MPa.m1/2 with 20 vol% ZrC addition, with an enhancement of 51% compared to the undoped ZTA mixture. The flexural strength, with a maximum of 1 121 MPa without ZrC addition and decreased to 645MPa with ZrC-10(vol%) addition, then increased monotonously to 1084 MPa as the ZrC content increased from 10 to 25 vol%.

Microstructure evolution, enhanced hardness and toughness in the solid-solution ceramic composite by reaction pressureless sintering of ZrB2 and TiC powders

In situ reaction and solid solution induced hardening in (Ti,Zr)B 2 ‐(Zr,Ti)C composites

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

Novel TiC-based composites with enhanced mechanical properties

Novel (Zr, Ti)B2-(Zr, Ti)C-SiC ceramics via reactive hot pressing

Microstructures and Enhanced Mechanical Properties of (Zr, Ti)(C, N)-Based Nanocomposites Fabricated by Reactive Hot-Pressing at Low Temperature

Reactive sintering behavior and enhanced densification of (Ti,Zr)B2–(Zr,Ti)C composites

Microstructures and mechanical properties of TiB2 composite ceramics with co-addition of Ti and TiC fabricated by SPS

Microstructure and mechanical behaviour of transient liquid phase spark plasma sintered B4C–SiC–TiB2 composites from a B4C–TiSi2 system

Microstructure and mechanical properties of SiC composite ceramics modified by (TixZr1–x)B2 solid solution

Microstructure and mechanical properties of TiB2–B4C ceramics fabricated by hot-pressing

Novel TiC-based ceramic with enhanced mechanical properties by reaction hot-pressing at low temperature

Study on the toughening mechanism of in-situ synthesis (TixZr1−x)B2 in solid-state sintered SiC composite ceramics

B4C‒TiB2 composite with modified microstructure and enhanced properties from optimal size coupling of raw powders

Effects of TiB2 Particles on the Microstructure Evolution and Mechanical Properties of B4C/TiB2 Ceramic Composite

Enhancement mechanical properties of in-situ preparated B4C-based composites with small amount of (Ti3SiC2+Si)

Toughening mechanism of B4C/TiB2 ceramic materials by in situ reaction via spark plasma sintering

Effects of ZrC content on the microstructure and mechanical property of ZrC/ZTA composites consolidated by hot pressing

Microstructure and mechanical properties of pressure‐less sintered B4C–SiC–ZrB2–LaB6 ceramic composites

The influence of Ti-induced precipitates on the microstructure and mechanical properties of (Zr,W)C solid solution

Microstructure and mechanical properties of Zn based composites reinforced by Ti3AlC2