Abstract:In the present work, effects of ZrC addition (10, 15, 20, 25 vol%) on microstructure and mechanical properties of ZTA20mol% (Zirconia-20mol% Toughened Alumina) ceramic composites were investigated. Samples were prepared by Hot Pressing Sintering (HP) at 1 600 ℃ and 30 MPa for a soaking time of 2 hours. Microstructures were characterized by XRD, Raman, SEM and TEM. XRD and Raman spectra results revealed that only ZrC, α-Al2O3 and ZrO2 were detected for all composites, indicating that these ceramic composites had excellent chemical compatibilities. SEM images showed refined microstructure was obtained, and the fracture surfaces exhibited a mixed process of transgranular and intergranular fracture. According to the TEM observations, some nano-sized ZrC particles dispersed inside Al2O3 grains and formed an intra/inter-type nanostructure. The relative densities and Vickers hardness were inversely proportional to ZrC content, which gradually decreased from 98.24% to 94.89%, from 1 847 to 1 691 HV1, respectively. Flexural strength and fracture toughness were tested by three-point bending method and single-edge notched beam method, respectively. The fracture toughness increased at first and then decreased with ZrC content increased from 0 to 25 vol%. The maximum value was 11.23 MPa.m1/2 with 20 vol% ZrC addition, with an enhancement of 51% compared to the undoped ZTA mixture. The flexural strength, with a maximum of 1 121 MPa without ZrC addition and decreased to 645MPa with ZrC-10(vol%) addition, then increased monotonously to 1084 MPa as the ZrC content increased from 10 to 25 vol%.

Microstructure and mechanical properties of Zn based composites reinforced by Ti3AlC2

Microstructure and Mechanical Properties of Ti2AlC-reinforced TiAl Composites

Microstructure characterization and mechanical properties of in situ synthesized Ti2(Al,Si)C reinforced Al composites

Microstructures and the improved mechanical properties of AZ91 alloy by incorporating Ti-6Al-4V particles

Microstructure, Mechanical, and Thermal Properties of in Situ-Synthesized (zrb2+sic)/zr2[al(si)]4c5 Composites

Microstructures and Enhanced Mechanical Properties of (Zr, Ti)(C, N)-Based Nanocomposites Fabricated by Reactive Hot-Pressing at Low Temperature

Microstructure and mechanical properties of TiC reinforced TZM composites prepared by spark plasma sintering

Microstructure, Mechanical Properties and Fracture Mechanism of Ti2AlC Reinforced AZ91D Composites Fabricated by Stir Casting

Effects of alloy elements (Mg, Zn) on the microstructure and mechanical properties of (TiC+TiB2)/Al composites

Preparation of in situ TiC@TiN core–shell and Ti2N–Al4C3 nanoparticles and their effects on Al–Zn–Mg–Cu alloy

Effects of ZrC content on the microstructure and mechanical property of ZrC/ZTA composites consolidated by hot pressing

Effect of Cu and Zn elements on morphology of ceramic particles and interfacial bonding in TiB2/Al composites

Effect of Ti particles on microstructure and mechanical properties of Mg–9Al–1Zn based composite sheets

Microstructure and mechanical properties of Ti3(Al,Ga)C2/Al2O3 composites prepared by in situ reactive hot pressing

Influence of Ti-6Al-4V particles on the interfacial microstructure and strength-ductility synergetic mechanism of AZ91 magnesium alloy

In Situ Preparation and Mechanical Properties of (ZrB2+ZrC)/Zr3[Al(Si)]4C6 Composites

Precipitation behavior and mechanical properties of Al-Zn-Mg-Cu matrix nanocomposites: Effects of SiC nanoparticles addition and heat treatment

Microstructure characterization and enhanced mechanical properties of quasi-continuous network structured Ti3AlC2-Al3Ti/2024Al composite

The Effect of Ti Particles Addition on the Microstructure and Mechanical Behavior of Mg AZ31/Al 6082 Composite Sheets

Microstructural characterization and mechanical properties of (TiC+TiB)/TA15 composites prepared by an in-situ synthesis method

Microstructure, mechanical properties and strengthening mechanism of in-situ synthesized TiC/6061 nanocomposites