Microstructure and mechanical properties of TiC reinforced TZM composites prepared by spark plasma sintering

Yanni Wei,Yu Chen,Shuhua Liang,Linghao Zhu,Yaru Li,Lei Jia

DOI: https://doi.org/10.1016/j.ijrmhm.2023.106345

IF: 4.804

2023-07-24

International Journal of Refractory Metals and Hard Materials

Abstract:In this paper, TiC (1 wt%, 5 wt%, 10 wt%, 15 wt%)-reinforced TZM composites with high relative density and good mechanical properties were prepared by high energy ball milling and spark plasma sintering. The microstructure, element distribution, and phase composition of TZM-TiC composites were systematically analyzed and characterized. The mechanical properties of TZM-TiC composites were evaluated by microhardness test, room temperature compression test and high temperature compression test. The results proved that with the increase of TiC content, the size of Mo grains in TZM-TiC composites was significantly inhibited, and the morphology of the reinforcement phase changed from a spherical shape to a long stripe shape. Mo was found to be partially amorphous in TZM-TiC composites, and various second phases (TiC, Ti and Mo 2 C) were found in the TZM-TiC composites. Through two-dimensional mismatch theory and first-principle calculations, the strengthening effect of Mo-Mo 2 C interface was much higher than that of Mo-TiC and MoTi interface. The generation of amorphous Mo, the grain refinement and the second phase strengthening together significantly improve the micro-Vickers hardness and compressive strength of TZM-(10%, 15%)TiC composites, which contributes to the Vickers hardness of TZM-15%TiC reaching 885.77 HV, and the compressive yield strength of TZM-10%TiC composite reaching 2169.7 MPa. Besides, the TZM-10%TiC composite exhibits excellent thermal stability, and its compressive yield strength at 600 °C reaches 1880.7 MPa.

materials science, multidisciplinary,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to prepare TiC - reinforced TZM composites with high relative density and good mechanical properties by adding TiC nanoparticles with different contents (1 wt%, 5 wt%, 10 wt%, 15 wt%) into TZM alloy using high - energy ball milling and spark plasma sintering techniques. The main purpose of the research is to explore the influence of TiC nanoparticles on the microstructure of the TZM matrix and their improvement effect on the mechanical properties of the composites, especially the enhancement of hardness and compressive strength. In addition, the research also focuses on the thermal stability of the composites under high - temperature conditions.

Specifically, the paper solves the problem through the following aspects:

1. **Microstructure analysis**: Through means such as scanning electron microscopy (SEM) and transmission electron microscopy (TEM), the microstructure, element distribution, and phase composition of TZM - TiC composites are systematically analyzed. The results show that with the increase of TiC content, the growth of Mo grains is significantly inhibited, the morphology of the strengthening phase changes from spherical to elongated, partial Mo becomes amorphous, and multiple second phases (TiC, Ti, and Mo₂C) are found in the composites.

2. **Mechanical property evaluation**: Through micro - hardness testing, room - temperature compression testing, and high - temperature compression testing, the mechanical properties of TZM - TiC composites are evaluated. The experimental results prove that with the increase of TiC content, the micro - Vickers hardness and compressive strength of the composites are significantly improved. For example, the micro - Vickers hardness of TZM - 15%TiC reaches 885.77 HV, and the compressive yield strength of TZM - 10%TiC reaches 2169.7 MPa. In addition, the compressive yield strength of the TZM - 10%TiC composite can still reach 1880.7 MPa at 600 °C, showing good high - temperature stability.

3. **Theoretical analysis and calculation**: Through two - dimensional misfit theory and first - principles calculations, the strengthening effect of the Mo - Mo₂C interface is studied. The calculation results show that the strengthening effect of the Mo - Mo₂C interface is much higher than that of the Mo - TiC and Mo - Ti interfaces. This further explains the mechanism of the improvement of the mechanical properties of the composites.

In summary, through experimental and theoretical analysis, this paper systematically studies the influence of TiC nanoparticles on the microstructure and mechanical properties of the TZM matrix, providing design criteria and theoretical basis for the preparation of high - performance nanoscale composites.