Novel TiC-based composites with enhanced mechanical properties

Sijia Huo,Yujin Wang,Mianyi Yao,Zhikun Zhang,Lei Chen,Hui Gu,Jiahu Ouyang,Yu Zhou

DOI: https://doi.org/10.1016/j.jeurceramsoc.2021.05.008

IF: 5.7

2021-09-01

Journal of the European Ceramic Society

Abstract:<p>Novel TiC-based composites were synthesized by reactive hot-pressing at 1800 °C for 1 h with ZrB₂ addition as a sintering aid for the first time. The effects of ZrB₂ contents on the phase composition, microstructure evolution, and mechanical properties were reported. Based on the reaction and solid solution coupling effects between ZrB₂ and TiC, the product ZrC may be partially or completely dissolved into the TiC matrix, and then phase separation within the miscibility gap is observed to form lamellar nanostructured ZrC-rich (Zr, Ti)C. The TiC-10 mol.% ZrB₂ (starting batch composition) exhibits good comprehensive mechanical properties of hardness 27.7 ± 1.3 GPa, flexural strength 659 ± 48 MPa, and fracture toughness of 6.5 ± 0.6 MPa m^1/2, respectively, which reach or exceed most TiC-based composites using ceramics as sintering aids in the previous reports.</p>

materials science, ceramics