Abstract:: In situ micro-TiB2/Cu cermets with a different TiB2 content (40, 50, and 60 vol %) were successfully fabricated by combustion synthesis (CS) and hot press consolidation in Cu-Ti-B systems. In addition, different contents of Cr and Zr were added to the Cu-Ti-B systems. The microstructure, mechanical properties, and abrasive wear properties of the TiB2/Cu cermets were investigated. As the ceramic content increased, the yield strength and compressive strength of the cermets were found to increase, while the strain decreased. An increase in load and abrasive particle size caused the wear volume loss of the TiB2/Cu cermets to increase. When the ceramic content was 60 vol %, the wear resistance of the TiB2/Cu cermets was 3.3 times higher than that of pure copper. The addition of the alloying elements Zr and Cr had a significant effect on the mechanical properties of the cermets. When the Cr content was 5 wt %, the yield strength, ultimate compressive strength, and microhardness of the cermets reached a maximum of 997 MPa, 1183 MPa, and 491 Hv, respectively. Correspondingly, when the Zr content was 5 wt %, those three values reached 1764 MPa, 1967 MPa, and 655 Hv, respectively, which are 871 MPa, 919 MPa, and 223 Hv higher than those of the unalloyed cermets. The wear mechanism of the in-situ TiB2/Cu cermets, and the mechanisms by which the strength and wear resistance were enhanced by the addition of Zr, were preliminarily revealed.

Addition Effect of ZrC Nano-powder on the Microstructure and Mechanical Properties of TiCN-based Cermets Prepared by Spark Plasma Sintering

Effect of Nano-Si3n4 Addition on the Microstructure and Mechanical Properties of Ticn-Based Cermets

Effect of SiC Nano-Whisker Addition on TiCN-based Cermets Prepared by Spark Plasma Sintering

Effect of ZrC nano-powder addition on the microstructure and mechanical properties of binderless tungsten carbide fabricated by spark plasma sintering

Influence of ZrC Addition on the Microstructure, Mechanical Properties and Oxidation Resistance of Ti(C,N)-based Cermets

Effects of the addition of multi-walled carbon nanotubes on the microstructure and properties of Ti(C,N)-based cermets prepared by spark plasma sintering

Spark plasma sintered WC-Ni cemented carbides with various contents of ZrC nano-powder

Effect of the Addition of Ultrafine Powders on the Microstructure and Mechanical Properties of TiCN-Based Cermets

Effect of Y2O3 Addition on the Microstructure and Mechanical Properties of TiCN-based Cermets

Effect of Cr2C3 addition on microstructure and mechanical properties of Ti(CN)-based cermets

Effects of Cr and Zr Addition on Microstructures, Compressive Properties, and Abrasive Wear Behaviors of in Situ TiB2/Cu Cermets

Effect of Cr<sub>2</sub>C<sub>3</sub> Addition on Microstructure and Mechanical Properties of Ti(CN)-Based Cermets

Effect of tin content on microstructures and mechanical properties of Ti(C,N)/NiCr cermets

Effect of Carbon Addition on the Densification Behavior, Microstructure Evolution and Mechanical Properties of Ti(C, N)-based Cermets

Preparation and properties of Ti(C,N)-based cermets with graphene nanosheet addition by spark plasma sintering

Effect of Tic Addition on the Microstructure and Mechanical Properties of Tin-Based Cermets

Ticn-Based Cermets Strengthened with Sic Nano-Whiskers by Spark Plasma Sintering

Effect of Ta, Nb and Zr Additions on the Microstructures and Mechanical Properties of 70 Vol% TiC/Al Cermets

Fabrication of Nanocomposite Ti(C,N)-based Cermet by Spark Plasma Sintering

Effect of Cr3C2 Addition on the Microstructure, Magnetic and Mechanical Properties of TiC–TiN–WC–C–Ni Cermets

Novel TiC-based composites with enhanced mechanical properties