Effect of nano-TiC addition on sinterability and mechanical properties of TiC high temperature ceramics

Xu Guangping,Song Yihua,He Jiangrong,Cheng Lixia,Xie Zhipeng

DOI: https://doi.org/10.3969/j.issn.1001-1935.2013.06.003

2013-01-01

Refractories

Abstract:TiC high temperature ceramics were prepared by spark plasma sintering method( firing at 1 600 ℃ for 5 min,50 MPa),adding nano-TiC( 0,10%,20%,50% and 90%,in mass,the same hereinafter) into TiC micropowders( about 3 μm) in order to research the effect of nano-TiC on the sinterability and me- chanical properties of TiC matrix. The sinterability,microstructure and mechanical properties were charac- terized by Archimedes method,SEM and indentation method,respectively. Effect of nano-TiC addition on the sinterability of TiC ceramics was discussed according to the changes on densification and microstruc- ture,and its influence on mechanical properties was discussed according to the hardness and fracture toughness. The results show that the dispersity of nano-TiC in the matrix mainly impacts the sinterability and mechanical properties of TiC ceramics; a low nano-TiC addition( 10%) leads to an excellent dispersity,im- proving the sinterability and mechanical properties of TiC ceramics; fine microstructures can be obtained by adding nano-TiC; with 10% nano-TiC,TiC ceramics have the highest fracture toughness,performing ob- vious toughening mechanisms such as crack deflection and bridging.