Abstract:In this study, Spark Plasma Sintering (SPS) was utilized to fabricate fine-grained cemented carbides, and an orthogonal experimental design was employed to examine the influence of holding temperature (1100 °C, 1200 °C, 1300 °C) and holding time (5, 10, and 15 min) on the performance of WC-10Co cemented carbide specimens. Compared with conventional sintering methods, this work achieved the production of samples with enhanced overall performance at lower temperatures and shorter durations. Specifically, under the conditions of a holding temperature of 1300 °C and a holding time of 5 min, the resulting specimens exhibited a density of 14.64 g/cm3, a hardness of 91.29 HRA, a fracture toughness of 16.39 MPa·m½, and a transverse rupture strength of 2398 MPa. The microstructural analysis revealed that as the holding temperature increased, the Co phase in the specimens underwent a transformation from its initial powder form to banded cobalt and subsequently to slit-shaped cobalt. It was found that the presence of banded cobalt effectively hinders crack propagation, whereas slit-shaped cobalt is more effective in preventing crack initiation, thus impacting the overall performance of the specimens. By analyzing the sintering curves and microstructures, the densification mechanisms during SPS sintering of WC-Co cemented carbides were elucidated. The study concluded that the state changes of the Co phase play a significant role in the densification behavior, final microstructure, and properties of the sintered material. These findings offer valuable insights for understanding and optimizing the SPS process.

Spark plasma sintered WC-Ni cemented carbides with various contents of ZrC nano-powder

Effect of ZrC nano-powder addition on the microstructure and mechanical properties of binderless tungsten carbide fabricated by spark plasma sintering

Phase Composition and Microstructure of Binderless Wc-Zrc Cemented Carbides Fabricated by Spark Plasma Sintering

Ultrafine Binderless WC-based Cemented Carbides with Varied Amounts of AlN Nano-Powder Fabricated by Spark Plasma Sintering

Addition Effect of ZrC Nano-powder on the Microstructure and Mechanical Properties of TiCN-based Cermets Prepared by Spark Plasma Sintering

Microstructure and Mechanical Properties of Nano-Size Zirconium Carbide Dispersion Strengthened Tungsten Alloys Fabricated by Spark Plasma Sintering Method

Ultrafine WC-Ni cemented carbides fabricated by spark plasma sintering

Effect of SiC Nano-Whisker Addition on WC–Ni Based Cemented Carbides Fabricated by Hot-Press Sintering

Microstructure and Mechanical Properties of Ultrafine WC–Ni–VC–TaC–cBN Cemented Carbides Fabricated by Spark Plasma Sintering

Ultrafine WC-Ni-SiCw Cemented Carbides Fabricated by Spark Plasma Sintering

Preparation and Mechanical Properties of WC-10 Ni3Al Cemented Carbides with Plate-Like Triangular Prismatic WC Grains

Effect of Carbon Content on the Microstructure and Properties of WC-CoCrFeNi Cemented Carbides

The Enhancement of the Microstructure and Mechanical Performances of Ultrafine WC-Co Cemented Carbides by Optimizing Cr2(C,N) Addition and WC Particle Sizes

Effect of Nano-AlN Addition on the Microstructure and Mechanical Properties of Binderless WC-VC-TaC-AlN Cemented Carbides

Effect of Additive Amount of Cr on Microstructure and Properties of Wc-9ni Cemented Carbides

Effect of titanium addition on microstructure and mechanical properties of WC-Ni<sub>3</sub>Al cemented carbide br

Preparation of WC-Co Cemented Carbide by Spark Plasma Sintering: Microstructure Evolution, Mechanical Properties and Densification Mechanism

Preparation and Properties of WC-TiC-Ni Cemented Carbide

Research on Nano-Grained Cemented Carbide Prepared by Spark Plasma Sintering

Microstructures and Properties of WC-10 wt.%CoCrFeNiAlx Composite Cemented Carbides

High-Entropy-Alloy CoFeNiCr Bonded WC-Based Cemented Carbide Prepared by Spark Plasma Sintering