Abstract:Ultrafine binderless WC-based cemented carbides with varied amounts of AlN nano-powder (0–16wt.%) were fabricated by spark plasma sintering at 1600°C under a pressure of 50MPa with the assistance of VC and TaC as WC grain growth inhibitors. The densification behavior, phase composition, microstructure and mechanical properties of the as-prepared samples were investigated. During sintering, rapid sample shrinkage started at about 1050°C and ended at about 1550°C. X-ray diffraction analysis revealed that an appropriate addition amount of AlN nano-powder would be of help to limit the formation of W2C phase and promote the formation of solid solution phase of (V,W)C2 during sintering. As the added fraction of AlN nano-powder increased, the relative density of the samples initially increased and then decreased, reaching its maximum of about 99.6% when 3–5wt.% AlN nano-powder was added. Scanning electron microscopy examination indicated that the average size of WC grains in the samples was about 0.7μm and with increasing added fraction of AlN nano-powder, the abnormal growth of WC grains was suppressed and their sizes were somewhat reduced. Both the sample hardness and flexural strength first increased and then decreased with increasing added fraction of AlN nano-powder, reaching the maximum hardness of about 2400 HV10 with 3wt.% AlN nano-powder and maximum flexural strength of about 1250MPa with 5wt.% AlN nano-powder, respectively. However, the fracture toughness slightly decreased from 7.5 to 6.3MPa·m1/2 with increasing added fraction of AlN nano-powder.

Ultrafine WC-Ni-SiCw Cemented Carbides Fabricated by Spark Plasma Sintering

Effect of SiC Nano-Whisker Addition on WC–Ni Based Cemented Carbides Fabricated by Hot-Press Sintering

Ultrafine WC-Ni cemented carbides fabricated by spark plasma sintering

WC-Ni-SiCw Alloys Prepared by Hot-Pressed Sintering

Spark plasma sintered WC-Ni cemented carbides with various contents of ZrC nano-powder

Phase Composition and Microstructure of Binderless Wc-Zrc Cemented Carbides Fabricated by Spark Plasma Sintering

Microstructure and Mechanical Properties of SiC Whisker Reinforced CoCrNi Medium Entropy Alloys

Effect of SiC Nano-Whisker Addition on TiCN-based Cermets Prepared by Spark Plasma Sintering

Microstructure and Mechanical Properties of Ultrafine WC–Ni–VC–TaC–cBN Cemented Carbides Fabricated by Spark Plasma Sintering

Effects of SiC addition on microstructure and properties of WC–6Co cemented carbide prepared by SPS

The Enhancement of the Microstructure and Mechanical Performances of Ultrafine WC-Co Cemented Carbides by Optimizing Cr2(C,N) Addition and WC Particle Sizes

Fabrication of ultrafine WC-based cemented carbide by spark plasma sintering

Microstructure and Mechanical Properties of HfC-SiC Ceramics Influenced by WC Addition

Ticn-Based Cermets Strengthened with Sic Nano-Whiskers by Spark Plasma Sintering

Preparation and mechanical properties of SiCw-reinforced WC-10Ni3Al cemented carbide by microwave sintering

Ultrafine Binderless WC-based Cemented Carbides with Varied Amounts of AlN Nano-Powder Fabricated by Spark Plasma Sintering

Influence of VC/Cr3C2 and Mixed Carbon Content on Microstructure and Properties of Ultrafine WC-0.5Co Cemented Carbide

Mechanical and Tribological Properties of SiC Whisker‐reinforced SiC Composites Via Oscillatory Pressure Sintering

Ultrafine grained WC-10FeCoCu cemented carbides doped with La 2 O 3 prepared by spark plasma sintering

Processing and mechanical properties of B4C-SiCw ceramics densified by spark plasma sintering

Comparative Study on Microstructure and Mechanical Properties of Coarse-grained WC-based Cemented Carbides Sintered with Ultrafine WC or (W+C) as Additives