WC-Ni-SiCw Alloys Prepared by Hot-Pressed Sintering

Xiaoyong Ren,Zhijian Peng,Huiyong Rong,Ying Peng,Zhiqiang Fu,Chengbiao Wang,Yue Wen,Longhao Qi,Hezhuo Miao

DOI: https://doi.org/10.4028/www.scientific.net/kem.512-515.928

2012-01-01

Key Engineering Materials

Abstract:WC-Ni-SiCw alloys were prepared through hot-pressed sintering by using WC, Ni, VC, TaC and SiC nano-whisker as raw materials. The influence of SiC whisker addition on the microstructure and mechanical properties of the as-prepared WC-Ni alloys was investigated. Except WC hard phase and Ni binder phase, no other phase was detected by X-ray diffraction. The observations by scanning electron microscope demonstrated that there were some micropores in the as-prepared materials, and their size and quantity increased with increasing amount of SiCw. Vickers hardness and flexural strength tests indicated that the bulk hardness of WC-Ni-SiCw alloys slightly decreased with increasing amount of SiCw; and the flexural strength increased at first and then decreased with increasing amount of SiCw. The alloys with 0.53 wt% SiCw presented the highest flexural strength of 1700 MPa.