Properties of Ti(C,N)-based cermets reinforced with ZrO2 whiskers deposited via sulfate flux at high temperatures
Yihang Fang,Xianrui Zhao,Mengxian Zhang,Guoping Du,Jianbo Wu,Hu Cheng,Shuangxi Xue,Yanqiu Huo,Ping Zhang,Tianle Wang,Puyou Ying
DOI: https://doi.org/10.1016/j.vacuum.2021.110336
IF: 4
2021-09-01
Vacuum
Abstract:<p>Ti(C,N)-based cermets were prepared by vacuum hot-pressing sintering enhanced by the second phase of ZrO<sub>2</sub> whiskers via sulfate flux. The effects of ZrO<sub>2</sub> whiskers on the material properties of Ti(C,N)-based cermets at high temperature are discussed, including the room temperature microstructure, high-temperature oxidation resistance, and microstructure and mechanical properties at high temperature. The experimental result indicated that the addition of ZrO<sub>2</sub> whiskers improves the bending strength, fracture toughness, and oxidation resistance of Ti(C,N)-based cermets at high temperature. At a temperature of 1000 °C, the hardness, flexural strength, fracture toughness and elasticity modulus of the cermets with 7.5 wt.% ZrO<sub>2</sub> whiskers were 9.32 GPa, 1032 MPa, 6.71 MPa·m<sup>1/2</sup> and 193.5 GPa, respectively. The high-temperature strength and toughness of Ti(C,N)-based cermets with ZrO<sub>2</sub> whiskers were weakened by the softening of grain boundaries, the decrease in elastic modulus, and oxidation. Conversely, the high-temperature strength and toughness of Ti(C,N)-based cermets were increased by maintaining the rod crystal shape of ZrO<sub>2</sub> whiskers at a high temperature, enhanced the elastic modulus of cermets through the whiskers, and improved oxidation resistance.</p>
materials science, multidisciplinary,physics, applied