Abstract:This paper reports the development of TiCN - Co - Cr3C2 - Si3N4 cermets modified with the addition of B4C. Cermets of three different compositions with varying B4C in TiCN - Co - Cr3C2 - Si3N4 were fabricated. The TiCN, Co, Cr3C2, Si3N4 and B4C powders in the combinations 80%TiCN-5%Co-5%Cr3C2–5%Si3N4–5%B4C; 75%TiCN-5%Co-5%Cr3C2–5%Si3N4–10%B4C; 70%TiCN-5%Co-5%Cr3C2–5%Si3N4–15%B4C were ground in a ball milling unit for six hours at a speed of 300 rpm at a ball-to-powder ratio of 10:1. The powders were then sintered in a vacuum hot press at a temperature of 1600 °C and a pressure of 50 MPa with soaking time of 90 min. For comparison purpose, 90%TiCN-5%Co-5%Cr3C2 cermet was prepared. The microstructure of the sintered cermets revealed the core-rim structure. The Vickers hardness test was done with a load of 10 Kg and for duration of 10 s. Fracture toughness was measured using the crack length data obtained from the hardness test using scanning electron microscopy. The cermet with a composition 75% TiCN-5%Co-5% Cr3C2–5% Si3N4–10% B4C produced higher hardness of 26.53 ± 0.56 GPa and fracture toughness of 10.29 ± 0.18 MPa m and 70% TiCN-5%Co-5% Cr3C2–5% Si3N4–15% B4C showed high fracture toughness value of 11.23 ± 0.09 MPa m with hardness value of 21.05 ± 0.10 GPa. The cermet composition 75% TiCN-5%Co-5% Cr3C2–5% Si3N4–10% B4C retained the hardness of 16.85 GPa even after annealing at 600 °C. The sintered cermets tend to form TiO2 which determines the hardness of the annealed cermets at a range of 600 °C – 1000 °C. The presence of these oxides tends to decrease the hardness. The wear test was performed taking the cermet as the pin material. The abrasive and adhesive wear mechanisms were dominant in the cermets. The harder precipitates formed tend to increase wear resistance by reducing the wear rate. The harder precipitates (TiN and TiB2) formed mainly due to the addition of Si3N4 and B4C, this addition promotes adhesive wear by a tribolayer formation.

Development of TiCN-Co-Cr3C2-Si3N4-based cermets with improved hardness and toughness for cutting tool applications

Effect of Si3N4 Additive on Microstructure and Mechanical Properties of Ti(C,N)-Based Cermet Cutting Tools

On the effects of B4C addition on the microstructure, mechanical properties, wear and thermal stability of TiCN- co -Cr3C2-Si3N4 cermets developed by vacuum hot pressing

Microstructure, mechanical property and cutting performance of (Ti,W)C/Mo/Co/Ni cermet tool material prepared by spark plasma sintering and high frequency induction heating

Preparation and properties of Ti(C,N)-based cermets with graphene nanosheet addition by spark plasma sintering

Microstructure and Mechanical Properties of TiC Reinforced NbC-Ni4VC4Mo2C Cermets

Preparation and cutting performance of Ti(C7, N3)/TiB2/WC cermet tool material

Effect of SiC Nano-Whisker Addition on TiCN-based Cermets Prepared by Spark Plasma Sintering

Ultra-High Hardness TiC-W-Ni Cermets Prepared by Spark Plasma Sintering of Ultra-Fine TiC Powder

Ticn-Based Cermets Strengthened with Sic Nano-Whiskers by Spark Plasma Sintering

Microwave Sintering of Ti(C, N)-based Cermet Cutting Tool Material

Improvement in Microstructure and Mechanical Properties of Ti(C, N) Cermet Prepared by Two-Step Spark Plasma Sintering

Synthesis and cutting performance of Al2O3@Ni-reinforced Ti(C,N) cermet by spark plasma sintering

Achieving hardness‐strength‐toughness synergy in (Ti, W, Mo, Cr)(C, N)‐based cermets

Evolution of microstructure and interfacial characteristics of complete solid-solution Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Effects of the addition of multi-walled carbon nanotubes on the microstructure and properties of Ti(C,N)-based cermets prepared by spark plasma sintering

Synthesis and characterization of extremely hard and strong (W,Ti,Ta)C cermet by spark plasma sintering

Fabrication, microstructure evolution, and mechanical properties of Ti(C,N)-HfN-WC-Ni-Mo cermets

Effect of Nano-Si3n4 Addition on the Microstructure and Mechanical Properties of Ticn-Based Cermets

Synthesis of TiB 2 /Ti(C,N) cermet by RSPS: formation mechanism, shrinkage behavior, and mechanical properties

Development of TiCN-based cermets: Mechanical properties and wear mechanism