Dong Wang,Tongxin Wang,Qinghua Wang,Bo Qiu,ZhiBao Li

DOI: https://doi.org/10.1016/j.ceramint.2022.10.329

IF: 5.532

2023-03-01

Ceramics International

Abstract:In this paper, a Ti(C7, N3)/TiB2/WC cermet tool material was prepared by plasma sintering. The components of the tool material and sintering process parameters were optimized through testing mechanical property. The cutting performance of the prepared tool was studied in the cutting experiment of 06Cr19Ni10 austenitic stainless steel. A comparison was made between the prepared tool and the commercial cermet tool SNMN120708. It is shown that when the volume fractions of TiB2 and WC were 20% and 15%, respectively, at the sintering temperature of 1550 °C and with the holding time of 30 min, the prepared tool would possess the flexural strength of 1096.45 Mpa, the hardness of 18.9 Gpa, the fracture toughness of 9.85 Mpa·m1/2 and the optimal cutting speed of 150 m/min. At the cutting speeds of 100 m/min and 150 m/min, the cutting distance of the developed tool was larger than that of SNMN120708. When the cutting speeds were 200 m/min and 250 m/min, the cutting distance of SNMN120708 tool was relatively large. The main wear mechanism of Ti(C7, N3)/TiB2/WC and SNMN120708 tool was adhesive wear, with no trace of abrasive wear.

materials science, ceramics