Shufen Li,Yabin Zhu,Jianlong Chai,Yiwen Liu,Lijuan Niu,Xing Gao,Peng Jin,Tielong Shen,Minghuan Cui,Zhiguang Wang,Erqing Xie
Abstract:<p>In the present work, effects of ZrC addition (10, 15, 20, 25 vol%) on microstructure and mechanical properties of ZTA20mol% (Zirconia-20mol% Toughened Alumina) ceramic composites were investigated. Samples were prepared by Hot Pressing Sintering (HP) at 1 600 ℃ and 30 MPa for a soaking time of 2 hours. Microstructures were characterized by XRD, Raman, SEM and TEM. XRD and Raman spectra results revealed that only ZrC, α-Al<sub>2</sub>O<sub>3</sub> and ZrO<sub>2</sub> were detected for all composites, indicating that these ceramic composites had excellent chemical compatibilities. SEM images showed refined microstructure was obtained, and the fracture surfaces exhibited a mixed process of transgranular and intergranular fracture. According to the TEM observations, some nano-sized ZrC particles dispersed inside Al<sub>2</sub>O<sub>3</sub> grains and formed an intra/inter-type nanostructure. The relative densities and Vickers hardness were inversely proportional to ZrC content, which gradually decreased from 98.24% to 94.89%, from 1 847 to 1 691 HV1, respectively. Flexural strength and fracture toughness were tested by three-point bending method and single-edge notched beam method, respectively. The fracture toughness increased at first and then decreased with ZrC content increased from 0 to 25 vol%. The maximum value was 11.23 MPa.m<sup>1/2</sup> with 20 vol% ZrC addition, with an enhancement of 51% compared to the undoped ZTA mixture. The flexural strength, with a maximum of 1 121 MPa without ZrC addition and decreased to 645MPa with ZrC-10(vol%) addition, then increased monotonously to 1084 MPa as the ZrC content increased from 10 to 25 vol%.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to explore the effects of different zirconium carbide (ZrC) contents on the microstructure and mechanical properties of zirconia - toughened alumina (ZTA) ceramic composites. Specifically, the researchers hope to systematically study its influence on ZTA 20 mol% composites by adding different volume percentages of ZrC (10, 15, 20, 25 vol%) in order to develop ceramic composites with broader application prospects.
### Main research questions:
1. **Microstructure changes**: How does the microstructure of ZTA composites change after adding different contents of ZrC? Including grain size, phase composition, etc.
2. **Mechanical property improvement**: How does the addition of ZrC affect the mechanical properties of ZTA composites, such as relative density, Vickers hardness, flexural strength and fracture toughness?
3. **Mechanism analysis**: Explain the physicochemical changes that occur inside the material after the addition of ZrC and the mechanism of its influence on mechanical properties, especially the phase - transformation toughening mechanism of ZrO₂.
### Research background:
- ZTA (Zirconia Toughened Alumina) ceramics are widely used in structural applications due to their excellent mechanical properties, wear resistance, good thermal characteristics and high corrosion resistance.
- Through different synthesis methods (such as spark plasma sintering, hot - press sintering, oscillatory pressure sintering, etc.), the fracture toughness of ZTA can reach 4 to 7 MPa m\(^{1/2}\).
- Many studies are dedicated to synergistically toughening ZTA ceramics by adding other components (such as SiC, TiC, NbC, etc.), but there is still a lack of detailed research on the effect of ZrC addition at present.
### Research methods:
- **Material preparation**: Samples were prepared by hot - press sintering method at 1600 °C and 30 MPa.
- **Characterization means**: XRD, Raman spectroscopy, SEM, TEM and other techniques were used to analyze the microstructure of samples; the flexural strength and fracture toughness were tested by three - point bending method and single - edge notched beam method.
### Main findings:
- **Microstructure**: With the increase of ZrC content, the grains of the composite were refined, and nano - scale ZrC particles were formed and dispersed inside the Al₂O₃ grains, forming an internal / external nano - structure.
- **Mechanical properties**:
- The relative density and Vickers hardness decrease with the increase of ZrC content.
- The fracture toughness first increases and then decreases, with the maximum value of 11.23 MPa m\(^{1/2}\), corresponding to 20 vol% ZrC addition.
- The flexural strength gradually increases when the ZrC content increases from 10 vol% to 25 vol%, and can reach up to 1084 MPa.
### Conclusion:
By adding ZrC, the fracture toughness of ZTA ceramic composites can be significantly improved, especially when 20 vol% ZrC is added, the best performance is shown. In addition, the addition of ZrC also promotes the phase - transformation toughening effect of ZrO₂, further improving the comprehensive mechanical properties of the material.