Effect of TZP nanoparticles synthesized by RCVD on mechanical properties of ZTA composites sintered by SPS

Qizhong Li,Yongfang Chen,Qingfang Xu,Meijun Yang,Song Zhang,Takashi Goto,Rong Tu

DOI: https://doi.org/10.1016/j.jeurceramsoc.2022.02.043

IF: 5.7

2022-07-01

Journal of the European Ceramic Society

Abstract:Alumina is an engineering ceramic material with excellent comprehensive properties as well as the inherent shortcoming of the low fracture toughness. Y2O3-stabilized t-ZrO2 (TZP) is an effective additive to improve its fracture toughness. In this work, rotary chemical vapor deposition (RCVD) was applied to uniformly coat TZP nanoparticles on α-Al2O3 powder, and then the powder was compacted via spark plasma sintering. The content of TZP increased from 0.56 to 4.7 wt% with increasing the deposition temperature from 500 to 800 °C but decreased at 900 °C. The RCVD-TZP nanoparticles homogeneously surrounded the α-Al2O3 grains and inhibited its growth after sintering. The relative density, fracture toughness and hardness of the ZTA composites had the maximum values of 99.2%, 7.28 ± 0.33 MPa m1/2, and 19.5 ± 0.5 GPa at 1500 °C and 4.7 wt% RCVD-TZP, respectively, much higher than the ZTA composites directly mixed with TZP commercial powder.

materials science, ceramics