Microstructure, Mechanical Properties, and Sintering Behavior of Ti3O-Fe2TiO4-TiC Composites
Tingting Zhang,Kangyan Fan,Yi Xu,Xinghua Yang,Yonghong Fu
DOI: https://doi.org/10.1007/s11665-024-09411-9
IF: 2.3
2024-04-10
Journal of Materials Engineering and Performance
Abstract:This study aims to assess the impact of TiC content on the sintering behavior, microstructure, and mechanical properties of Ti 3 O-Fe 2 TiO 4 composites produced by the reactive spark plasma sintering (SPS) technique. The powders of Ti 3 O, Ti, Fe, and TiC were utilized as the starting materials, sintered by SPS under 1500 °C at 45 MPa for 7 min. The high relative density of 97.16% was achieved for the maximum TiC content (namely 30 vol.%). X-ray diffraction patterns and microstructural observations endorsed the in situ formation of Fe 2 TiO 4 compound during the SPS process. Because this phase has a low melting point, its presence could activate the liquid phase sintering mechanism, promoting the sintering behavior of the as-sintered composites. In addition, when more TiC content was added to the composite matrix, the fracture mode changed from intergranular to mixed-mode. In terms of mechanical properties, the highest macro-hardness (13.29 GPa), micro-hardness (1244.84 HV 0.3 kg ), and bending strength (601 MPa) were achieved by the composite containing the highest proportion of TiC within the tested range.
materials science, multidisciplinary