Abstract:WC-Co cemented carbides are widely used in the fields of military, aerospace, mining and cutting industry etc. In this paper, a new two-step method for the preparation of WC-Co cemented carbides was proposed. First, the mixture of yellow tungsten trioxide (WO3) and cobaltic oxide (Co2O3) were reduced by carbon black to remove all the oxygen. Then, the carbothermic reduction products were precisely mixed with an appropriate amount of carbon black to directly prepare WC-Co cemented carbides. The effects of C/WO3 ratio on the phase composition, morphological evolution, particle size and mechanical properties of products are investigated. The experimental results revealed that when the C/WO3 molar ratio was above 2.7, all oxygen in the raw material mixture were removed by carbon black and a mixture of W2C and η-phase were obtained after the first step of carbothermic reduction at 1150 °C for 2 h; then, the mixture of carbothermic reduction product and an appropriate content of carbon black was compacted, and the green compact was first carbonized at 1200 °C for 2 h and then sintered at 1450 °C for 4 h to prepare cemented carbides. With the increase of C/WO3 ratio at the first stage, the content of η-phase with a low melting point increased, which resulted in the large grain size of WC in the finally prepared cemented carbide. Compared with the traditional method of preparing cemented carbides, the cemented carbides prepared by the current method showed a higher hardness and toughness. Furthermore, the addition of a proper content of the VC in the second stage can significantly inhibit the grain growth of WC and further increase the hardness of cemented carbides.

A Review of the Preparation Methods of WC Powders

Preparation Technology of Ultra-Fine Tungsten Carbide Powders: an Overview

A short and facile process to synthesize WC-Co cemented carbides

Ultrafine/nano WC-Co Cemented Carbide: Overview of Preparation and Key Technologies

Rapid synthesis of ultrafine WC-Co cemented carbides by in-situ reactions and spark plasma sintering

Effect of WC-Ni Powder Composition and Preparation on Cold Spray Performance

Preparation of nano-scaled WC powder by low-temperature carbothermic reduction method

Study on influencing factors and mechanism of high-quality tungsten carbide nanopowders synthesized via carbothermal reduction

Preparation of Ultra-Fine WC-Co Cermet and Its Wear Behavior

Additive manufacturing of WC-Co cemented carbides: process, microstructure, and mechanical properties

On the fabrication of ultrafine-grained potassium-doped tungsten: Mechanical milling and spark plasma sintering of K-doped W powder prepared by evaporation-condensation method

A Novel Method for Direct Synthesis of WC-Co Nanocomposite Powder

Fabrication of spherical WC-Co powders by radio frequency inductively coupled plasma and a consequent heat treatment

Preparation, properties and microstructure of high hardness WC-co cemented carbide tool materials for ultra-precision machining

Preparation Method of Porous Tungsten

High-gravity Combustion Synthesis and in Situ Melt Infiltration: A New Method for Preparing Cemented Carbides

Research on Preparation Methods of Ultra-coarse WC Particles

Cemented Tungsten Carbide Hardmetal-An Introduction

Preparation and characterization of high-performance in-situ synthesized WC reinforced nickel-based coatings

Synthesis and Sintering of Tungsten and Titanium Carbide: A Parametric Study

Preparation and characterization of W@WCx composite powder by oxidation-vacuum carbonization process