Abstract:WC-Co cemented carbides are widely used in the fields of military, aerospace, mining and cutting industry etc. In this paper, a new two-step method for the preparation of WC-Co cemented carbides was proposed. First, the mixture of yellow tungsten trioxide (WO3) and cobaltic oxide (Co2O3) were reduced by carbon black to remove all the oxygen. Then, the carbothermic reduction products were precisely mixed with an appropriate amount of carbon black to directly prepare WC-Co cemented carbides. The effects of C/WO3 ratio on the phase composition, morphological evolution, particle size and mechanical properties of products are investigated. The experimental results revealed that when the C/WO3 molar ratio was above 2.7, all oxygen in the raw material mixture were removed by carbon black and a mixture of W2C and η-phase were obtained after the first step of carbothermic reduction at 1150 °C for 2 h; then, the mixture of carbothermic reduction product and an appropriate content of carbon black was compacted, and the green compact was first carbonized at 1200 °C for 2 h and then sintered at 1450 °C for 4 h to prepare cemented carbides. With the increase of C/WO3 ratio at the first stage, the content of η-phase with a low melting point increased, which resulted in the large grain size of WC in the finally prepared cemented carbide. Compared with the traditional method of preparing cemented carbides, the cemented carbides prepared by the current method showed a higher hardness and toughness. Furthermore, the addition of a proper content of the VC in the second stage can significantly inhibit the grain growth of WC and further increase the hardness of cemented carbides.

Preparation and characterization of W@WCx composite powder by oxidation-vacuum carbonization process

In-situ synthesis of core-shell structure W(WC) composite grains in W-Cu composites fabricated by infiltration

Preparation of Ultra-Fine WC-Co Cermet and Its Wear Behavior

Synthesis and Formation Mechanism of W/TiC Composite Powders by a Wet Chemical Route

Effect of Co on morphology and preparation of in situ synthesis of WC-Co composite powders

Preparation Technology of Ultra-Fine Tungsten Carbide Powders: an Overview

A facile route to prepare ODS WC Co cemented carbides

Study on the preparation mechanism of novel WC-Cr2(C, N)-Co nanocomposites

Preparation and properties of W-Mo-Cu composite using solution combustion synthesized W Mo solid solution nanopowder

A short and facile process to synthesize WC-Co cemented carbides

Preparation and characterization of high-performance in-situ synthesized WC reinforced nickel-based coatings

A novel approach to fabricate WC reinforced W Cu composites via MSC and infiltration method

Microstructure and properties of W Cu composites reinforced by in-situ generated WC

PREPARATION OF ULTRAFINE W–Cu COMPOSITE POWDER USING ULTRASONIC-ASSISTED ELECTROLESS PLATING

Preparation and Properties of Fine-Grained and Ultrafine-Grained W-TiC-Y2O3 Composite

Oxidative Ablation Behavior of W‐Coated C/C Composites Prepared by Chemical Vapor Deposition with Heat Treatment

Study of a New Method to Fabricate W–Cu Composites

Preparation of Wo3/C Composite and Its Application in Oxidative Desulfurization of Fuel

Preparation of nano-scaled WC powder by low-temperature carbothermic reduction method

WC-VC/Cr3C2 composite powders prepared by a carbothermic reduction-carburization process

Mechanism of the early stages of oxidation of WC–Co cemented carbides