Abstract:To improve the strength and toughness of conventional particle‐reinforced iron matrix composites, a novel W@WC/Fe core–shell bar‐reinforced iron matrix composites (CBIMCs) which has an architecture similar to concrete is synthesized by casting and in‐situ solid‐phase diffusion method. The W@WC/Fe core–shell bar is constituted by a core of residual W bar and a shell of gradient‐structured WC‐Fe layer. To improve the strength and toughness of conventional particle‐reinforced iron matrix composites, W@WC/Fe core–shell bar‐reinforced iron matrix composites (CBIMCs) are synthesized by casting and in‐situ solid‐phase diffusion method. These composites, which have an architecture similar to concrete, consist of a core of residual W bar and a shell of gradient‐structured WC‐Fe layer. The effect of in‐situ solid diffusion time on the evolution of microstructure and mechanical properties of the composites is investigated. It is observed that for in‐situ solid diffusion times ranging from 3 to 24 h, the reinforcement in the composites remained as W@WC/Fe core–shell bars. As the solid diffusion time increased, the diameter of the W core gradually decreased, and the thickness of the WC‐Fe shell layer increased. At a solid diffusion time of 30 h, the reinforcement transitioned to the WC‐Fe composite bar. Additionally, with longer solid diffusion times, the WC particles transformed from a triangular prism shape to a truncated octahedron. The composite prepared at 18 h exhibits the highest ultimate compression strength and strain, reaching values of 1100 ± 18 MPa and 35.5 ± 1.3%, respectively. This excellent ultimate compression strength is mainly due to the WC particles, which enhanced load transfer strengthening and dislocation strengthening. Moreover, the metal W core and iron matrix effectively hinder microcrack propagation, thus contributing to the enhanced toughness of the composite.

Microstructure and properties of W Cu composites reinforced by in-situ generated WC

Long-term Ball Milling and Hot Pressing of In-Situ Nanoscale Tungsten Carbides Reinforced Copper Composite and Its Characterization

Influences of Ni/Cu/Cr3C2 Composite Additive on Microstructure and Properties of WC–10Co Fine Grained Hardmetal

Microstructure and Properties of In-Situ TiC Reinforced Copper Nanocomposites Fabricated Via Long-Term Ball Milling and Hot Pressing

Enhanced the Mechanical Properties and Corrosion Resistance of Ultra-Coarse Grain WC-8Co Cemented Carbides by the Introduction of Cu and Ni

In-situ synthesis of core-shell structure W(WC) composite grains in W-Cu composites fabricated by infiltration

A novel approach to fabricate WC reinforced W Cu composites via MSC and infiltration method

Cold-sprayed Cu Matrix Composite Coatings with Core-Shell Structured Co@WC Reinforcements on Q235 Steel

Study of Microstructure of Coarse-grain Tungsten Carbide Composite Produced by In-Situ Metallurgy Reaction

Mechanical and tribological properties of WC particles reinforced Cu-20Zn matrix composites

Insight into the Microstructure and Tensile Behavior of the W–Cu Composite Reinforced with Tungsten Fibers and Particulates

Microstructural evolution and performance analysis of WC-11Co reinforced iron matrix composites

Tribological and Electrochemical Corrosion Behaviors of Cu-based Powder Metallurgy Composites Reinforced by In-Situ WC with Different Morphology

Effect of carburized time on microstructure and properties of W Cu composites fabricated by vacuum pulse carburization

Microstructure and Mechanical Properties Evolution of W@WC/Fe Core–Shell Bar‐Reinforced Iron Matrix Composites: Effect of In‐situ Solid Diffusion Time

Microstructure and high-temperature mechanical properties of Cu-W composite prepared by hot isostatic pressing

Effect of WC mass fraction on the microstructure and frictional wear properties of WC/Fe matrix composites

Fabrication and microstructure of W-Cu composites prepared from Ag-coated Cu powders by electroless plating

Comparative Study on Microstructure and Mechanical Properties of Coarse-grained WC-based Cemented Carbides Sintered with Ultrafine WC or (W+C) as Additives

Influence of TiC Content on Microstructure and Properties of W-3OCu/TiC Composites

Effect of Particle Size on Microstructure and Element Diffusion at the Interface of Tungsten Carbide/High Strength Steel Composites