Abstract:Three-dimensional (3D) SiC/SiCf composites were fabricated by a polymer impregnation and pyrolysis (PIP) method using 3D four directional braided preforms from two kinds of SiC fibers as the reinforcements and liquid polycarbosilane as the SiC precursor.Both kinds of SiC fibers were prepared from the same precursor and process but with different heat treatment temperatures.The one prepared at a higher temperature (No.1) had a higher crystallinity than the another one (No.2).A thin pyrolytic carbon (PyC) interlayer was coated on the preforms by a methane CVD method before impregnation.Their microstructures and mechanical properties were investigated by TEM,SEM,Raman spectroscopy and mechanical tests.Results showed that both had a polycrystalline structure with grain sizes of 8-15 nm.Fiber pullout was seen from the fracture cross-section of the composites after a bending test,indicating pseudo-ductile fracture behavior.The composite using No.1 SiC fibers had an average flexural strength,elastic modulus and fracture toughness of 955.0±42.8 MPa,110.3 ± 1.7 GPa and 28.5 ±2.8 MPa· m1/2,respectively,which are Superior to those of the material formed using No.2 SiC fibers.This was ascribed to the high modulus and excellent thermal resistance of the stoichiometric No.1 SiC fibers.The PyC layer adhering to No.1 SiC fibers was ordered and smooth while that deposited on No.2 SiC fibers had a loose and granular microstructure,which was attributed to the different surface chemistries of the two types of SiC fibers.

Fabrication And Mechanical Properties Of Sicf/Sic Composites Via Polycarbosilane Pyrolysis

Fabrication and mechanical properties of SiCf/SiC composites via polycarbosllane pyrolysis

Processing and Characterization of C-F/Sic Composites

Fabrication, Microstructures and Properties of SiCf/SiC Composites Prepared with Two Kinds of SiC Fibers As Reinforcements

Study of Properties of Silicon Carbide Fiber Reinfoced Si-O-C Composites Using Low Cost Polysiloxane

High Performance SiC/SiOC Composites with in Situ Carbon Interface

2.5-DIMENSION SiCf/SiC COMPOSITES FABRICATED BY LOW PRESSURE CHEMICAL VAPOR INFILTRATION

Microstructure and Mechanical Properties of Three-Dimensional Carbon/Silicon Carbide Composites Fabricated by Chemical Vapor Infiltration

MECHANICAL PROPERTY OF 2.5 DIMENSIONAL SILICON CARBIDE FIBER REINFORCED SILICON CARBIDE COMPOSITES

Mechanical Property And Toughening Mechanism Of 2.5d C/C-Sic Composites With High Textured Pyrocarbon Interface

Influence of polycarbosilane composition on the properties of SiC/SiC composite fabricated by precursor infiltration and pyrolysis process

Fabrication and characterization of 2.5D and 3D SiCf/SiC composites

Fabrication of Cf/SiC composites by precursor infiltration and pyrolysis process

Fabrication Process and Properties of Silicon Carbide Fiber Reinforced Si-O-C Composites Using Polysiloxane As Precursor

Mechanical, Thermal, and Dielectric Properties of SiCf/SiC Composites Reinforced with Electrospun SiC Fibers by PIP

Microstructure and Mechanical Properties of SiC and Carbon Hybrid Fiber Reinforced SiC Matrix Composite

Effects of In-Situ Carbon Layer and Volume Fraction of SiC Fiber on the Mechanical Properties and Fracture Behaviors of SiCf/SiC Composites Fabricated by a Modified PIP Method

High-performance 3D SiC/PyC/SiC Composites Fabricated by an Optimized PIP Process with a New Precursor and a Thermal Molding Method

Mechanical Properties of SiC/SiC Composites by PIP Process with a New Precursor at Elevated Temperature

Processing and Properties of 2D SiC/SiC Composites by Precursor Infiltration and Pyrolysis

Mechanical and Dielectric Properties of SiC F /sic Composites Fabricated by PIP Combined with CIP Process