Abstract:By conducting combustion synthesis in high-gravity field, the solidified TiC-TiB2 with a series of TiB2 mole content were prepared through adjusting the mole ratio of C and B elements in combustion system. XRD, FESEM and EDS results showed that with increasing TiB2 mole content, the matrix of TiC-TiB2 composite ceramics transformed a number of fine TiB2 platelets from the TiC spherical grains, and fine-grained even ultrafine-grained microstructures were achieved in solidified TiC-50%TiB2 due to the coupled quasi-eutectic growth under rapid solidification of the ceramic. Properties showed that relative density, Vickers hardness and flexural strength of TiC-50%TiB2 simultaneously reached the maximum values of 98.7%, 21.5 +/- 1.5 GPa and 860 +/- 35 MPa, whereas the maximum fracture toughness of 13.5 +/- 1.5 MPa m(0.5) was achieved in TiC-66.7%TiB2. FESEM fractography analyses of the solidified ceramics indicated that the highest flexural strength achieved in TiC-50%TiB2 benefits from not only the lowest content of Al2O3 inclusions and Cr-W-Ti borides, but also the achievements of fine-grained microstructure in the near-full-density ceramic and high fracture toughness contributed from a intensive coupled mechanism of crack deflection, crack-bridging and pull-out by a large number of fine TiB2 platelets. (C) 2012 Elsevier B.V. All rights reserved.

Combustion synthesis of Ti(C, N) TiB2 composite powders under super gravity conditions

Combustion Synthesis of Ti(C,N)-TiB_2 Composite Powders under Super Gravity Conditions

Combustion Synthesis of Ti<sub>3</sub>SiC<sub>2</sub>/TiC Composites from Elemental Powders under High-Gravity Conditions

In Situ Combustion Synthesis of TiB<sub>2</sub>-AIN Composites

Combustion Synthesis of TiCxN1−x–TiB2 Ceramic Composites in a High-Gravity Field

Combustion synthesis of Ti3SiC2 under high-gravity condition

Combustion synthesis of porous TiC/Ni composites under high gravity

Effect of TiB_2 content on microstructure and mechanical properties of in-situ fabricated TiB_2/B_4C composites

Microstructure Transformation and Mechanical Properties of TiC–TiB2 Ceramics Prepared by Combustion Synthesis in High Gravity Field

Effect of reactant Ti/B4C ratio on the stoichiometry and mechanical properties of h-BN–Ti(C,N) prepared by combustion synthesis

Large-Scale Solidified Tib2-(Ti,W)C Composite Ceramics Prepared By Combustion Synthesis Under High Gravity

Preparation and characterization of TiB2-Al2O3 composite powder by combustion synthesis process

Large-scale (Ti,Cr)B2-Cu composite by combustion synthesis

Combustion Synthesis of Ti(C,N) Powder

Combustion Synthesis of TiB2-TiC/42CrMo4 Composites with Gradient Joint Prepared in Different High-Gravity Fields

Microstructure Modification and Fracture Behavior of Solidified TiC–TiB2 Ceramic Prepared by Combustion Synthesis in Ultra-High Gravity Field

Large-Scale (Ti,Cr)B<sub>2</sub>-Cu Composite by Combustion Synthesis

PREPARATION OF TIB2/TIC CERAMIC COMPOSITES BY HIGH-GRAVITY COMBUSTION SYNTHESIS

Preparation of Tib2 Nanoparticles Reinforced Cu-Matrix Composite by Direct Combustion Synthesis

Effects of Supergravity Conditions on Combustion Synthesis of NiAl Intermetallies