Abstract:By conducting combustion synthesis in high-gravity field, the solidified TiC-TiB2 with a series of TiB2 mole content were prepared through adjusting the mole ratio of C and B elements in combustion system. XRD, FESEM and EDS results showed that with increasing TiB2 mole content, the matrix of TiC-TiB2 composite ceramics transformed a number of fine TiB2 platelets from the TiC spherical grains, and fine-grained even ultrafine-grained microstructures were achieved in solidified TiC-50%TiB2 due to the coupled quasi-eutectic growth under rapid solidification of the ceramic. Properties showed that relative density, Vickers hardness and flexural strength of TiC-50%TiB2 simultaneously reached the maximum values of 98.7%, 21.5 +/- 1.5 GPa and 860 +/- 35 MPa, whereas the maximum fracture toughness of 13.5 +/- 1.5 MPa m(0.5) was achieved in TiC-66.7%TiB2. FESEM fractography analyses of the solidified ceramics indicated that the highest flexural strength achieved in TiC-50%TiB2 benefits from not only the lowest content of Al2O3 inclusions and Cr-W-Ti borides, but also the achievements of fine-grained microstructure in the near-full-density ceramic and high fracture toughness contributed from a intensive coupled mechanism of crack deflection, crack-bridging and pull-out by a large number of fine TiB2 platelets. (C) 2012 Elsevier B.V. All rights reserved.

Combustion Synthesis of TiCxN1−x–TiB2 Ceramic Composites in a High-Gravity Field

Combustion synthesis of porous TiC/Ni composites under high gravity

Combustion Synthesis of Ti<sub>3</sub>SiC<sub>2</sub>/TiC Composites from Elemental Powders under High-Gravity Conditions

Microstructure Transformation and Mechanical Properties of TiC–TiB2 Ceramics Prepared by Combustion Synthesis in High Gravity Field

Combustion synthesis of Ti(C, N) TiB2 composite powders under super gravity conditions

Combustion synthesis of Ti3SiC2 under high-gravity condition

Combustion Synthesis of Ti(C,N)-TiB_2 Composite Powders under Super Gravity Conditions

Microstructure Modification and Fracture Behavior of Solidified TiC–TiB2 Ceramic Prepared by Combustion Synthesis in Ultra-High Gravity Field

Combustion Synthesis of TiB2-TiC/42CrMo4 Composites with Gradient Joint Prepared in Different High-Gravity Fields

Self-Propagating High-Temperature Synthesis (SHS) of Ti-Containing Ceramic Composites under Ultra-High Gravity

Microstructures and Toughening of TiC-TiB2Ceramic Composites with Cr-Based Alloy Phase Prepared by Combustion Synthesis in High-Gravity Field

In Situ Combustion Synthesis of TiB<sub>2</sub>-AIN Composites

Large-Scale Solidified Tib2-(Ti,W)C Composite Ceramics Prepared By Combustion Synthesis Under High Gravity

Preparation of Al2O3-ZrO2-SiO2 ceramic composites by high-gravity combustion synthesis

PREPARATION OF TIB2/TIC CERAMIC COMPOSITES BY HIGH-GRAVITY COMBUSTION SYNTHESIS

Microstructure and mechanical properties regulation and control of in-situ TiC reinforced CoCrFeNiAl0.2 high-entropy alloy matrix composites via high-gravity combustion route

Microstructures, Densification and Mechanical Properties of TiC–Al2O3–Al Composite by Field-Activated Combustion Synthesis

High-Gravity Combustion Synthesis of Al2tio5/Mullite Ceramic Composites

Self-propagating high temperature combustion synthesis of TiC/TiB2 ceramic–matrix composites

Rapid Preparation Of Mgal2o4 Ceramics By High-Gravity Combustion Synthesis

Fabrication of Densified YAG Ceramics by Combustion Synthesis under Ultra-High Gravity