Microstructure and mechanical properties regulation and control of in-situ TiC reinforced CoCrFeNiAl0.2 high-entropy alloy matrix composites via high-gravity combustion route
Guannan Zhang,Xiao Yang,Yi Zhao,Zengchao Yang,Jiangtao Li
DOI: https://doi.org/10.1016/j.jallcom.2021.163221
IF: 6.2
2022-04-01
Journal of Alloys and Compounds
Abstract:In this study, CoCrFeNiAl0.2(TiC)x (x = 0,0.06,0.12,0.2) composites were prepared by high-gravity combustion synthesis (HGCS). The mixture powders of several low-cost metal oxides (Co2O3, Cr2O3, Fe2O3, NiO), Al, Ti and C were used as raw materials. In the high-gravity field, the CoCrFeNiAl0.2 high-entropy alloys (HEAs) were obtained by inducing a thermic reaction between the several low-cost metal oxides (Co2O3, Cr2O3, Fe2O3, NiO) and Al powders. Then the TiC was in-situ synthesized by Ti and C powders. The results show that the size and distribution of the in-situ synthesized TiC can be controlled by adjusting the Ti and C additions and the value of high-gravity field. When the high-gravity field rises to 1200 g, the bending strength, compressive strength and specific strength of CoCrFeNiAl0.2(TiC)0.12 composites respectively up to 1.17 GPa, 2.13 GPa, 0.3 MPa·Kg−1·m−3. Therefore, the HGCS with ‘green’ and efficiency characteristics offers an alternative pathway to control the structure and properties of the ceramic/ HEAs composites.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering