The Combustion Synthesis Of Si3n4-Tin-Sic Multiphase Ceramics

Gq Chen,Jc Han,Sy Du
2001-01-01
Abstract:The Si3N4-TiN-SiC multiphase ceramics was produced by combustion synthesis with powders of TiSi2 and SiC. The nitride mechanism of TiSi2 was studied: the phases of TiN and Si were firstly formed and then Si was synthesised with nitrogen gas to Si3N4. The density, hardness and bending strength of the ceramic are 3.01 g/cm(3), 78(HRA) and 250 Mpa respectively.