Preparation and characterization of TiB2-Al2O3 composite powder by combustion synthesis process

Zhiqiang Yu,Zhenguo Yang

DOI: https://doi.org/10.3321/j.issn:1002-185x.2005.11.034

2005-01-01

Rare Metal Materials and Engineering

Abstract:The combustion synthesis reaction with reductive process was used to produce TiB2-Al2O3 composite powders from TiO2-B2O3-Al system. The phase, the chemical composition and the macrostructure were analyzed by XRD, XPS and SEM. The microstructure of the composite powders was characterized by TEM and HREM. The results show that the TiB2-Al2O3 composite powders could be obtained by combustion synthesis method between 420 degrees C similar to 700 degrees C. The composite powder was made up of TiB2 and Al2O3 only, the particle distribution was uniform. Because of the good interface formation, between TiB2 and Al2O3 particle during the synthesis reaction, which made TiB2 particles separated each other by Al2O3 particles and could inhibit effectually the grain growth in the particles and finally lead to decrease in the particle size, their,mean particle size was in the range of 3 mu m similar to 5 mu m.