Abstract:Aluminum nitride–boron nitride (AlN–BN) composites were prepared based on the nitridation of aluminum boride (AlB2). AlN powder was added to change the BN volume fraction in the obtained composites. Thermogravimetry–differential thermal analysis (TG-DTA), X-ray diffractometry, and the nitridation ratio were used to investigate the nitridation process of AlB2. At ∼1000°C, a sharp exothermic peak occurred in the DTA curve, corresponding to the rapid nitridation of aluminum in AlB2. On the other hand, the nitridation of the transient phase, Al1.67B22, was very slow when the temperature was 1600°C. The pressure of the nitrogen atmosphere was also an important factor; high nitrogen pressure remarkably promoted nitridation. Treatment at 2000°C was disadvantageous for nitridation, because of the rapid formation of a dense surface layer that inhibited nitrogen diffusion into the specimen interior. Three specimens, with 5 wt% Y2O3 additive and different BN contents, were prepared by pressureless reactive sintering, according to the determined sintering schedule. Electron microscopy (scanning and transmission) observations revealed that the in-situ-formed BN flakes were homogeneously and isotropically distributed in the AlN matrix. A schematic mechanism for microstructural formation was developed, based on the results of nitridation and the microstructural features of the obtained composites. The obtained composites, with a low BN content, exhibited a high bending strength, comparable to that of reported hot-pressed AlN–BN composites.

Reaction synthesis of high performance boron nitride-containing composites (BNCC)

Reaction Synthesis of Ceramic Composites Containing In Situ Formed Boron Nitride as Dispersed Phase

Nonoxide–boron Nitride Composites: in Situ Synthesis, Microstructure and Properties

In Situ Combustion Synthesis of TiB<sub>2</sub>-AIN Composites

Reaction Synthesis of Aluminum Nitride-Boron Nitride Composites Based on the Nitridation of Aluminum Boride

Reactive synthesis of alumina-boron nitride composites

Reaction-Bonded Boron Nitride-Aluminum Nitride Ceramic Composites

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Fabrication of Boron Nitride Dispersed Nanocomposites by Chemical Processing and Their Mechanical Properties

Fabrication of Silicon Nitride/ Boron Nitride Nanocomposite Powder

Sialon-Boron Nitride Porous Composites: in Situ Synthesis, Microstructure and Properties

Fabrication and properties of AL2O3-SiAlON composites with nano-sized t- and h-BN dispersion

Silicon Nitride/Boron Nitride Composite by Combustion Synthesis

The Properties and Preparation Methods of Different Boron Nitride Nanostructures and Applications of Related Nanocomposites

In Situ Reaction Synthesis of Silicon Carbide–Boron Nitride Composite from Silicon Nitride–Boron Oxide–Carbon

Boron Nitride?Aluminum Nitride Ceramic Composites Fabricated by Transient Plastic Phase Processing

Synthesis of SiC/BN nanocomposite powders by carbothermal reduction and nitridation of borosilicate glass, and the properties of their sintered composites

Synthesis and characterization of cubic boron nitride (Al)-Al2O3 composites under high pressure and high temperature conditions

Synthesis of h‐BN composite powders via aluminothermic reduction combustion route

Preparation of Sic/Bn Nanocomposite Powders by Chemical Processing

Preparation and Properties of Cubic BN Sintered Compact with AlN.