Abstract:As an advanced connection technology for large thick-walled components, narrow gap laser welding has the advantages of small heat input and high efficiency and quality. However, porosity defects are prone to occur inside the weld due to the complex welding environment. In this study, the influence of the process parameters and pollutants such as water and oil on the porosity defect were explored. The action mechanism of water on the electron temperature and spectral intensity of the laser-induced plasma was analyzed. The results showed that the spectral intensity during narrow gap laser welding was weaker than that of flat plate butt welding. Under the optimal welding process conditions, the electron temperature during narrow gap laser self-fusion welding was calculated as 7413.3 K by the Boltzmann plot method. The electron density was 5.6714 × 1015 cm−3, conforming to the thermodynamic equilibrium state. With six groups of self-fusion welding parameters, only sporadic porosity defects were observed according to the X-ray detection. When there was water on the base metal surface, a large number of dense pores were observed on the weld surface and in the weld through X-ray inspection. Compared with the spectral data obtained under the normal process, the relative light intensity of the spectrometer in the whole band was reduced. The electron temperature decreased to the range of 6900 to 7200 K, while the electron density increased. The spectrum variation during narrow gap laser wire filling welding was basically the same as that of laser self-fusion welding. The porosity defects caused by water and oil pollutants in the laser welding could be effectively identified based on the intensity of the Fe I spectral lines.

The Characteristics and Reduction of Porosity in High-Power Laser Welds of Thick AISI 304 Plate

The Elimination of Pores in Laser Welds of AISI 304 Plate Using Different Shielding Gases

Investigation on Porosity Suppression in Deep-Penetration Laser Welding by Using Computational Fluid Dynamics

Porosity Sensitivity of A356 Al Alloy During Fiber Laser Welding

Experimental Investigation and Numerical Study on the Elimination of Porosity in Aluminum Alloy Laser Welding and Laser–GMA Welding

Mitigation of Porosity Defects in Fiber Laser Welding under Low Vacuum

Investigation on the Effects of Shielding Gas on Porosity in Fiber Laser Welding of T-joint Steels

Porosity Formation Mechanism in Laser Spot Microwelding of Pt-Ir Alloy and 316L Stainless Steel Wires

Reducing the Porosity in Die-Cast Magnesium Alloys During Laser Welding

Porosity Formation Mechanism and Its Prevention in Laser Lap Welding for T-Joints

Repression of porosity with beam weaving laser welding

Porosity inhibition of aluminum alloy by power-modulated laser welding and mechanism analysis

Microstructure and Properties of High-Power Laser Welding of Sus304 to Sa553 for Cryogenic Applications

Mitigation of porosity in adjustable-ring-mode laser welding of medium-thick aluminum alloy

Investigation of the Inhibition Mechanism of Process Porosity in Laser-MIG Hybrid-Welded Joints for an Aluminum Alloy

Metallurgical and Mechanical Properties of Underwater Laser Welds of Stainless Steel

Thermal and Fluid Flow Characteristics and their Relationships with Porosity in Laser Welding of AA5083

Numerical study of keyhole dynamics and porosity formation during high‐power oscillating laser welding of medium‐thick aluminum alloy plates

Investigation of Weld Root Defects in High-Power Full-Penetration Laser Welding of High-Strength Steel

Underwater local dry cavity laser welding of 304 stainless steel

Study on Porosity Defect Detection in Narrow Gap Laser Welding Based on Spectral Diagnosis