Abstract:Because of their low density, high strength-to-weight ratio and high damping capacity, magnesium alloys have gained increasing applications in many fields, especially for die-cast magnesium alloys. The application of die-cast magnesium alloys in structures and repair welding of casting defects necessitates the development of welding techniques. As a high energy density thermal source, laser welding can reduce many welding defects compared with conventional welding methods, but pore formation during welding of die-cast magnesium alloys is still a severe problem that has not been solved. This paper seeks to identify the mechanism of pore formation during laser welding of die-cast magensium alloys and search for a metallurgic solution of porosity. The great tendency to pore formation in die-cast magnesium alloys is attributed to high gas content in the base metal. The characteristic of gas source in die-cast magnesium alloys and the process of pore formation during laser welding are studied by some experiments including analysis of characteristic parameters of pores (porosity, average diameter and number densities), change of densities before and after heating (350 degrees C, holding time 1 h) and pore formation tendency under different vacuo heating conditions (heating the base metal to 350 degrees C under vacuum environment of different holding time). The results show that heating increases porosity, average diameter and number densities, which lead to the reduction of bulk density. Vacuo heating before welding can reduce porosity to a great extent, and with holding time prolonging, porosity reduces. In die casting, there are molecular hydrogen and atomic hydrogen in die-cast magnesium alloys. The hydrogen gas (molecular hydrogen) in high pressure pores in the base metal expands sharply in the molten pool, and the oversaturated atomic hydrogen can also form new pores or contribute to the growth of exsisting pores. That is to say that both molecular hydrogen and atomic hydrogen contribute to the pore formation of die-cast magnesium alloys during laser welding. During vacuo heating before welding, atomic hydrogen can escape in part through diffusion, thus reducing the tendency to form pores. With holding time of vacuo heating prolonging, the amount of atomic hydrogen escaping from the base metal increases, thus porosity reduces. Adding elements, which can combine hydrogen to form hydride, may be a possible solution to pore formation in die-cast magnesium alloys. Preliminary experiments show that adding Zr to welds during welding can reduce the tendency to form pores obviously, the reason for this needs further research.

Reducing the Porosity in Die-Cast Magnesium Alloys During Laser Welding

Effects of Welding Parameters on Weld Porosity During CO2 Laser Welding of Die-Cast Magnesium Alloys

EXPERIMENTAL STUDY ON THE REASON OF PORE FORMATION IN LASER WELDING OF DIE-CAST MAGNESIUM ALLOY

Experimental Study on Pores in Laser Welding of Magnesium Alloys

Formation Regularity of Pores During Laser Welding of Die-Cast Magnesium Alloys and Its Mechanism

Research status and prospect on porosity during laser welding of magnesium alloy

Porosity inhibition of aluminum alloy by power-modulated laser welding and mechanism analysis

Coupled effect of ultrasonic vibration and post-weld remelting on the porosity and microstructure of die-cast magnesium alloy AZ91D

Investigation of the Inhibition Mechanism of Process Porosity in Laser-MIG Hybrid-Welded Joints for an Aluminum Alloy

Mitigation of porosity in adjustable-ring-mode laser welding of medium-thick aluminum alloy

Mechanism analysis on suppressing porosity in laser-MIG hybrid welding of aluminum alloy via external magnetic field

Effect of filler materials on the porosity formation of aluminum alloy by laser welding with filler wire

Investigation on Porosity Suppression in Deep-Penetration Laser Welding by Using Computational Fluid Dynamics

Effect of ambient pressure on laser welding of AlSi10Mg fabricated by selected laser melting

Effect of magnetic field orientation on suppressing porosity in steady-magnetic-field-assisted aluminum alloy deep-penetration laser welding

The effect of laser oscillation welding on porosity suppression for medium-thick Al alloy with high Mg content

Numerical study of keyhole dynamics and porosity formation during high‐power oscillating laser welding of medium‐thick aluminum alloy plates

Mechanism of pore suppression in aluminum alloy laser-MIG hybrid welding based on alternating magnetic field

Repression of porosity with beam weaving laser welding

Investigation of Pore Reduction in Hybrid Joints of Conventionally and Additively Manufactured AlSi10Mg Using Electron Beam Welding

Oxygen content and morphology of laser cleaned 5083 aluminum alloy and its influences on weld porosity