Abstract:Aiming to solve the serious porosity defects in laser welded girth joints of thin-walled tube and end plug made of nano-sized Ce2O3 doped Mo alloy (NC-Mo), the influences of laser power modulation, multipass remelting and zirconium (Zr) addition on the number, size and distribution of porosity defects were experimentally studied. By utilizing X-ray computed tomography (XCT), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS) analysis, transmission electron microscope (TEM) and Raman spectrum (RS), the porosity feature of welded joints achieved under various conditions was analyzed. The results showed that welding cycles had a significant influence on the porosity ratio of fusion zone (FZ) while the amplitude and frequency of laser power waveform slightly influenced the porosity. When the welding cycles increased from 2 to 8, the porosity ratio of FZ decreased from about 1.00% to about 0.48% and the maximum and average pore diameters reduced by about 53% and 27%, respectively. Adding minor Zr in molten pool can further reduce the R-p of FZ to about 0.35%. Through analysis, it can be seen that the pores in FZ can be divided into irregularly-shaped keyhole-induced pores and spherical metallurgy-induced pores. The latter was generated possibly because some impurity elements (including O and H) pre-existing in base metal (BM). Increasing welding cycles can promote the gas in molten pool to float and outflow, thus significantly decreasing the porosity. Moreover, Zr added in molten pool can be preferentially reacted with O to generate ZrO2, which can inhibit the precipitation of volatile MoO2 to thus suppress the generation of metallurgy-induced pores.

Repression of porosity with beam weaving laser welding

Improvement of Weld Quality Using A Weaving Beam in Laser Welding

Investigation on Porosity Suppression in Deep-Penetration Laser Welding by Using Computational Fluid Dynamics

Effects of Welding Parameters on Weld Porosity During CO2 Laser Welding of Die-Cast Magnesium Alloys

Porosity Sensitivity of A356 Al Alloy During Fiber Laser Welding

Experimental Investigation and Numerical Study on the Elimination of Porosity in Aluminum Alloy Laser Welding and Laser–GMA Welding

Mitigation of Porosity Defects in Fiber Laser Welding under Low Vacuum

Numerical simulation on pore formation and suppression for dual-beam laser welding of sandwich structure

The Characteristics and Reduction of Porosity in High-Power Laser Welds of Thick AISI 304 Plate

Porosity inhibition of aluminum alloy by power-modulated laser welding and mechanism analysis

Effect of beam oscillation frequency on porosity in laser welding of aluminum alloy lap-butt joints

Reducing the Porosity in Die-Cast Magnesium Alloys During Laser Welding

MECHANISMS OF THE POROSITY FORMATION DURING THE FIBER LASER LAP WELDING OF ALUMINIUM ALLOY

Effect of welding stability on process porosity in laser arc hybrid welding of dissimilar steel

Effect of ambient pressure on laser welding of AlSi10Mg fabricated by selected laser melting

Effects of Power Modulation, Multipass Remelting and Zr Addition Upon Porosity Defects in Laser Seal Welding of End Plug to Thin-Walled Molybdenum Alloy

Prevention and mechanical analysis of porosity formation in pulsed CO2 laser welding of 30CrMnSiA

Experimental Study on Pores in Laser Welding of Magnesium Alloys

Porosity Formation Mechanism and Its Prevention in Laser Lap Welding for T-Joints

Investigation on the Effects of Shielding Gas on Porosity in Fiber Laser Welding of T-joint Steels

Formation Regularity of Pores During Laser Welding of Die-Cast Magnesium Alloys and Its Mechanism