Abstract:Nanocrystalline Ni thin film exhibits poor thermo-mechanical properties due to its unstable microstructure at elevated temperature. Here, the paper endows a new approach to solve above issue via addition of nano-multilayers and incorporation of W for nanocrystalline Ni-based films, to provide novel Ni/Ni3Al-W nano-composite multilayered structure with high hardness and good thermal stability. The thermal evolution of microstructure and mechanical properties was investigated to reveal nano crystalline stability and strengthening mechanisms for co-sputtered Ni/Ni3Al-W multilayers with varied W concentrations and annealing temperature. The lamellar structure and nonequilibrium phases are well maintained in 600 degrees C annealed multilayers, while nano-grains are further refined with increasing W addition. Annealing at 800 degrees C results in the appearance of elemental redistribution and phase separation in multilayers, leading to the layered structure dissolved and globular W-related particles precipitated. Annealing hardening is founded in most of annealed Ni/Ni3Al-W multilayers. Based upon microstructure observation, grain boundary relaxation and W-related phase precipitation are mainly responsible for the hardness enhancement of multilayers at 600 degrees C and 800 degrees C, respectively. Notably, the best hardness is achieved at the value of 15.6 GPa for 800 degrees C annealed 12.5 at% W doped Ni/Ni3Al-W multilayer, which shows the residual layer interfaces with larger precipitations in microstructure. This hardness increment for annealed Ni-based multilayers can be attributed that the high degree of strengthening is provided by a combination of hardening precipitation and survived lamellar structure via the Orowan mechanisms, offering a feasible insight to develop nano-metallic coatings for further increasing thermo-mechanical properties. (C) 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Effect of Isothermal Annealing on Grain Size and Microhardness of Ni-P and Ni-W-P Platings

Effect of High Temperature Annealing on the Microstructure and Thermal Shock Resistance of Tungsten Coatings Grown by Chemical Vapor Deposition

Preparation and Properties of Textured Ni–W Coatings Electrodeposited on the Steel Surface from a Pyrophosphate Bath

Effects of annealing temperature on the crystal structure and properties of electroless deposited Ni–W–Cr–P alloy coatings

The W alloying effect on thermal stability and hardening of nanostructured Cu-W alloyed thin films

Effect of Tungsten on Microstructures of Annealed Electrodeposited Ni-W Alloy and Its Corrosion Resistance

Mechanical and Tribological Properties of Ni-B and Ni-B-W Coatings Prepared by Electroless Plating

Investigations on the Influence of Annealing on Microstructure and Mechanical Properties of Electrodeposited Ni-Mo and Ni-Mo-W Alloy Coatings

Microstructure and wear properties of crystalline W alloy coatings prepared by electrodeposition

Corrosion resistance of electrolessly deposited Ni–P and Ni–W–P alloys with various structures

Influence of Annealing on the Microstructure and Mechanical Properties of Ni-W/Boron Composite Coatings

Wear and Corrosion Properties of Crystalline Ni-W Alloy Coatings Prepared by Electrodeposition

Comparative Study on Microstructure and Properties of Electroless Ni-P and Ni-W-P Coatings

The Research on Technology of Electroless Ni-W-P Ternary Alloys Plating on the Aluminium Alloy

Enhancement of Hardness and Thermal Stability of W-doped Ni3Al Thin Films at Elevated Temperature

Evolution of Microstructure and Mechanical Properties of Electroplated Nanocrystalline Ni–Co Coating During Heating

Effect of W Content on the Structure and Corrosion Resistance of Ni-W Alloy Plates

Study on property of electroless plating Ni-W-P coating

Enhancement of High-Temperature Strength of Ni-Based Films by Addition of Nano-Multilayers and Incorporation of W

Coating process conditions of W alloy electrodeposition

Fabrication, thermal stability and microhardness of sputtered Ni–P–W coating