Effect of W Content on the Structure and Corrosion Resistance of Ni-W Alloy Plates

Gong Rui,Liu Lin

DOI: https://doi.org/10.3321/j.issn:1002-185x.2008.01.031

2008-01-01

Rare Metal Materials and Engineering

Abstract:The Ni-W alloy plates were prepared by electro-deposition on copper substrate using nickel sulphate and sodium tungstate as precursors. The structure and morphology of the electrodeposited plates as well as microhardness were investigated by X-ray diffraction(XRD), X-ray fluorescence system (XRF), optical microscopy (OM) and micro-indentation. It is found that the structure and hardness of the plates are closely related to W content. The plates are of crystalline structure when W content is less than 21 at%, but of amorphous structure when W above the value. Especially, the plate exhibits a columnar crystalline structure when W content is around 20 at%. The microhardness increases continuously with the increase of W content. Both columnar and amorphous plates grew well on the copper substrate and exhibited a high hardness of above HV 5800 MPa. Finally, the corrosion resistance of the Ni-W plates with different W contents was examined by electrochemical polarization in a 3% NaCl solution open to air. It is found that the columnar and amorphous plates also displayed excellent corrosion resistance as indicated by a wider passive region and a lower corrosion current density as compared with 1Cr18Ni9T stainless steel.