Abstract:The spinning cup, a crucial component of textile equipment, relies heavily on 2A12 aluminum alloy as its primary raw material. Commonly, electroplating and chemical nickel-phosphorus (Ni-P) plating are employed to improve the surface characteristics of the object. Nevertheless, due to the growing expectations for the performance of aluminum alloys, the hardness and wear resistance of Ni-P coatings are no longer sufficient to fulfill industry standards. This study primarily focuses on the synthesis of Ni-B-PTFE nanocomposite chemical plating and its effectiveness when applied to the surface of 2A12 aluminum alloy. We examine the impact of the composition of the plating solution, process parameters, and various other factors on the pace at which the coating is deposited, the hardness of the surface, and other indicators of the coating. The research findings indicate that the composite co-deposited coating achieves its optimal surface morphology when the following conditions are met: a nickel chloride concentration of 30 g/L, an ethylenediamine concentration of 70 mL, a sodium borohydride concentration of 0.6 g/L, a sodium hydroxide concentration of 90 g/L, a lead nitrate concentration of 30 mL, a pH value of 12, a temperature of 90 °C, and a PTFE concentration of 10 mL/L. The coating exhibits consistency, density, a smooth surface, and an absence of noticeable pores or fissures. The composite co-deposited coating exhibits a surface hardness of 1109 HV0.1, which significantly surpasses the substrate's hardness of 232.38 HV0.1. The Ni-B-PTFE composite coating exhibits an average friction coefficient of around 0.12. It has a scratch width of 855.18 μm and a wear mass of 0.05 mg. This coating demonstrates superior wear resistance when compared to Ni-B coatings. The Ni-B-PTFE composite coating specimen exhibits a self-corrosion potential of -6.195 V and a corrosion current density of 7.81 × 10-7 A/cm2, which is the lowest recorded. This enhances its corrosion resistance compared to Ni-B coatings.

The Research on Technology of Electroless Ni-W-P Ternary Alloys Plating on the Aluminium Alloy

The Research on Coating of Electroless Ni-W-P Ternary Alloys

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Study on Electroless Plating Ni-W-P Ternary Alloy with High Tungsten from Compound Complexant Bath

Preparation and Properties of Textured Ni–W Coatings Electrodeposited on the Steel Surface from a Pyrophosphate Bath

Mechanical properties of Ni-based coatings fabricated by electroless plating method

Coating process conditions of W alloy electrodeposition

Wear and Corrosion Properties of Crystalline Ni-W Alloy Coatings Prepared by Electrodeposition

Microstructure and wear properties of crystalline W alloy coatings prepared by electrodeposition

A Method for Electroless Nickel Plating on Aluminum Alloy Surface

Electroless deposition of ternary Ni–P alloy coatings containing tungsten or nano-scattered alumina composite on steel

Electrodeposition of Ni-W Alloy in Sulphate System

Composite Electroless Nickel-nano Al2O3 Coatings on Steel Substrate

Mechanical and Tribological Properties of Ni-B and Ni-B-W Coatings Prepared by Electroless Plating

Influences of Heat Treatment Process on Properties of Electroless Plating Ni-W-Mo-P Alloy

Influence of Plating Temperature on the Morphology,Hardness and Corrosion Resistance of Electroless Ni-P Alloy Plating

Corrosion resistance of electrolessly deposited Ni–P and Ni–W–P alloys with various structures

Ni-B-PTFE Nanocomposite Co-Deposition on the Surface of 2A12 Aluminum Alloy

Fabrication, thermal stability and microhardness of sputtered Ni–P–W coating

Recent Progress in Electrodeposition of Ni and Ni-based Alloys

Study on Heat Transfer Performance and Anti-Fouling Mechanism of Ternary Ni-W-P Coating