Abstract:A Ni–W alloy coating with a thickness of 5 μm was electroplated on N80 steel, and its electrochemical performance in a 3.5% NaCl solution was investigated. The atomic models of passive films and corrosion mechanism were analysed with the density functional theory calculation. The results show that the electroplated Ni–W alloy coating is composed of W atoms in the Ni lattice, and its surface roughness and particle size are 66.1 and 640.4 nm, respectively. The corrosion current density of Ni–W coating is lower than that of the substrate, indicating better corrosion resistance, while the corrosion potential is opposite, which is more passive than the substrate. The total impedance of Ni–W coating is higher than that of the substrate, which is attributed to the formation of NiO passive film during the corrosion process. On a déposé par galvanoplastie un revêtement en alliage Ni-W d'une épaisseur de 5 μm sur l'acier N80 et l'on a examiné ses performances électrochimiques dans une solution de NaCl à 3.5%. On a analysé les modèles atomiques des films passifs et le mécanisme de corrosion au moyen du calcul de la théorie fonctionnelle de la densité. Les résultats montrent que le revêtement électrolytique en alliage Ni–W est composé d'atomes de W dans le réseau de Ni et que sa rugosité de surface et sa taille de particules sont respectivement de 66.1 et 640.4 nm. La densité de courant de corrosion du revêtement en Ni–W est inférieure à celle du substrat, indiquant une meilleure résistance à la corrosion, alors que le potentiel de corrosion est à l'opposé, ce qui est plus passif que le substrat. L'impédance totale du revêtement en Ni–W est supérieure à celle du substrat, ce qui est attribué à la formation d'un film passif de NiO pendant le procédé de corrosion.

Coating process conditions of W alloy electrodeposition

Effect of Process Parameters on Microstructure and Properties of AlCoCrFeNi-WC-WS2 Composite Coating Prepared by Laser Cladding

Microstructure and wear properties of crystalline W alloy coatings prepared by electrodeposition

Preparation and Properties of Textured Ni–W Coatings Electrodeposited on the Steel Surface from a Pyrophosphate Bath

Wear and Corrosion Properties of Crystalline Ni-W Alloy Coatings Prepared by Electrodeposition

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

The Research on Coating of Electroless Ni-W-P Ternary Alloys

The Research on Technology of Electroless Ni-W-P Ternary Alloys Plating on the Aluminium Alloy

Composite Electroless Nickel-nano Al2O3 Coatings on Steel Substrate

Microstructure, electrochemical corrosion and corrosion mechanism of electroplated Ni–W alloy coating by DFT calculation

Investigation of the Enhancement Mechanism of Electrochemically Deposited Ni–Co–W Coatings via Laser Irradiation: Effect of W Contents on Corrosion Resistance

Preparation, characterisation and electrochemical study of crack-free nanocrystalline electrodeposited Co-W alloy coating of high hardness

Study on Electroless Plating Ni-W-P Ternary Alloy with High Tungsten from Compound Complexant Bath

Excellent Properties of Ni-15 wt.% W Alloy Electrodeposited from a Low-Temperature Pyrophosphate System

Effect of Rare Earth on the Microstructure and Performance of Electrodeposited Ni-W Coatings

Mechanical and Tribological Properties of Ni-B and Ni-B-W Coatings Prepared by Electroless Plating

Influence of Electrodeposition Process Parameters and Si3N4 Nanoparticle Concentration on Microhardness and Wettability of Ni-Co-Si3N4 Nanocomposite Coatings

Electrodeposition of Ni-W-P alloy

Effect of Heat Treatment on Microstructure and Corrosion Resistance of Electrodeposited Nickel-Tungsten Alloy Coating

Influences of Co and process parameters on structure and corrosion properties of nanocrystalline Ni-W-Co ternary alloy film fabricated by electrodeposition at low current density

Electrodeposition of nanocrystalline Ni-W coatings with citric acid system