Abstract:A series of Fe-Mn/Al2O3 catalysts were prepared and studied for low temperature selective catalytic reduction (SCR) of NO with NH3 in a fixed-bed reactor. The effects of Fe and Mn on NO conversion and the deactivation of the catalysts were studied. N2 adsorption-desorption, X-ray diffraction, transmission electron microscopy, energy dispersive spectroscopy, H2 temperature-programmed reduction, NH3 temperature-programmed desorption, X-ray photoelectron spectroscopy (XPS), thermal gravimetric analysis and Fourier transform infrared spectroscopy were used to characterize the catalysts. The 8Fe-8Mn/Al2O3 catalyst gave 99% of NO conversion at 150 °C and more than 92.6% NO conversion was obtained in a wide low temperature range of 90–210 °C. XPS analysis demonstrated that the Fe3+ was the main iron valence state on the catalyst surface and the addition of Mn increased the accumulation of Fe on the surface. The higher specific surface area, enhanced dispersion of amorphous Fe and Mn, improved reduction properties and surface acidity, lower binding energy, higher Mn4+/Mn3+ ratio and more adsorbed oxygen species resulted in higher NO conversion for the 8Fe-8Mn/Al2O3 catalyst. In addition, the SCR activity of the 8Fe-8Mn/Al2O3 catalyst was only slightly decreased in the presence of H2O and SO2, which indicated that the catalyst had better tolerance to H2O and SO2. The reaction temperature was crucial for the SO2 resistance of catalyst and the decrease of catalytic activity caused by SO2 was mainly due to the sulfate salts formed on the catalyst.

Selective Catalytic Reduction of NO by NH3 Over Fresh and Sulfated CuO/gamma-Al2O3 Catalysts

Insights into the Effects of Sulfate Species on CuO/TiO2 Catalysts for NH3-SCR Reactions

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Activation of Fast Selective Catalytic Reduction of NO by NH3 at Low Temperature over TiO2 Modified CuOX-CeOX Composites

Low temperature SCR denitration with NH3 by highly dispersed Ni–Cu Sites: An insight into surface acidity and redox ability

Surface Tailoring on Bifunctional CuOx/MnO2 Catalyst to Promote the Selective Catalytic Reduction of NO with NH3 and Oxidation of CO with O2

Low-temperature selective catalytic reduction of NO on CeO2-CuO/Al2O3 catalysts prepared by different methods

Fe-Mn/Al2O3 Catalysts for Low Temperature Selective Catalytic Reduction of NO with NH3

Selective catalytic reduction of NO(x)with NH(3)over TiO(2)supported metal sulfate catalysts preparedviaa sol-gel protocol

DRIFT Study of CuO-CeO₂-TiO₂ Mixed Oxides for NOx Reduction with NH₃ at Low Temperatures.

Reaction Pathway Investigation on the Selective Catalytic Reduction of NO with NH3 over Cu/SSZ-13 at Low Temperatures.

Selective Catalytic Reduction Of Nox With Nh3 At Low Temperatures Over Metal Oxide Supported On Ac-C Cellular Monoliths

DRIFT Study of CuO–CeO2–TiO2 Mixed Oxides for NOx Reduction with NH3 at Low Temperatures

Selective Catalytic Reduction of NO over Cu-Mn/OMC Catalysts: Effect of Preparation Method

The Superior Performance of Nb-modified Cu-Ce-Ti Mixed Oxides for the Selective Catalytic Reduction of NO with NH3 at Low Temperature

In situ regeneration of sulfated Cu/SAPO-34 catalyst for the selective catalytic reduction of NOx with NH3

Selective catalytic reduction of nitric oxide with carbon monoxide over alumina-pellet-supported catalysts in the presence of excess oxygen

Structure, Acidity and Activity of CuOx/WOx–ZrO2 Catalyst for Selective Catalytic Reduction of NO by NH3

Improvement of Catalytic Activity over Cu-Fe Modified Al-Rich Beta Catalyst for the Selective Catalytic Reduction of Nox with Nh3

Ni-Mn Bi-Metal Oxide Catalysts for the Low Temperature SCR Removal of NO with NH3

Selective catalytic reduction of NO with NH3 over CuOX-carbonaceous materials