Abstract:NO and CO are two primary pollutants in the sintering flue gas emission, posing significant challenges for the treatment. Under oxygen-enriched conditions, CO was easily oxidized to CO2 before participating in CO-SCR reaction as a reducing agent. Consequently, NH3-SCR technology coupled with CO oxidation reaction is a promising approach for simultaneous NO and CO removal. In this study, a series of bifunctional CuOx/MnO2 catalysts were synthesized using a combine of hydrothermal and wet impregnation methods, and their catalytic performance for simultaneous removal of NO and CO was assessed. CuOx/alpha-MnO2 catalyst displayed outstanding catalytic activity for both NO and CO, achieving over 80 % NO removal efficiency and 96 % CO conversion rate at 150 degrees C, while CuOx/beta-MnO2 catalyst exhibited poor catalytic activity in the entire temperature range. Moreover, the interplay between the NH3-SCR and CO catalytic oxidation reactions was also explored. XPS results revealed that the concentration of Mn4+ and Cu+ species significantly influenced the catalytic activity of the catalysts for the simultaneous removal of NO and CO. Particularly, the presence of Mn4+ species promoted "fast SCR" reaction, whereas Cu+ species demonstrated higher reactivity for both NO reduction and CO oxidation. In situ DRIFTS analysis of transient reactions revealed that the L-H mechanism was followed over CuOx/alpha-MnO2 catalyst in the NH3-SCR reaction, while both the M -K and L-H mechanisms were observed in CO catalytic oxidation reaction.

Selective catalytic reduction of NO with NH3 over CuOX-carbonaceous materials

Tailoring the Proceeding of the NH3-SCO and NH3-SCR Reactions over FeOx Catalysts by Modifying with NbOx

Activation of Fast Selective Catalytic Reduction of NO by NH3 at Low Temperature over TiO2 Modified CuOX-CeOX Composites

Selective catalytic reduction of NOX with ammonia over Mn–Ce–OX/TiO2-carbon nanotube composites

Catalytic Reduction of NO by NH3 over Fe–Cu–OX/CNTs-TiO2 Composites at Low Temperature

Low temperature selective catalytic reduction of NOx by NH3 over Cu modified V2O5/TiO2–carbon nanotube catalyst

Selective catalytic reduction of NO by NH3 over CuO–CeO2 in the presence of SO2

In Situ Supported Mnox-Ceox On Carbon Nanotubes For The Low-Temperature Selective Catalytic Reduction Of No With Nh3

The Role of Surface Properties of Activated Carbon in the Catalytic Reduction of NO by Carbon

Structure, Acidity and Activity of CuOx/WOx–ZrO2 Catalyst for Selective Catalytic Reduction of NO by NH3

Experimental Investigation into the Denitrification Performance of a CuO/AC Catalyst Used for NO Reduction with Ammonia

Effect of Pretreatment Method of Activated Carbon on the Catalytic Reduction of NO by Carbon over CuO

Surface Tailoring on Bifunctional CuOx/MnO2 Catalyst to Promote the Selective Catalytic Reduction of NO with NH3 and Oxidation of CO with O2

Simultaneous removal of NO x and SO 2 by low-temperature selective catalytic reduction over modified activated carbon catalysts

CuOx and WOx modified CeO2-TiO2 with various morphologies for the selective catalytic reduction of NOx with NH3

High-performance Fe-Cu composite oxide for selective catalytic reduction of NO with NH3: Driving of Cu on α-Fe2O3

Cr–MnO Mixed-Oxide Catalysts for Selective Catalytic Reduction of NO with NH3 at Low Temperature

Selective Catalytic Reduction Of Nox With Nh3 At Low Temperatures Over Metal Oxide Supported On Ac-C Cellular Monoliths

Highly active and stable Cu Fe /AC-H catalysts with CuFe2O4 for NO reduction by CO in the presence of H2O and SO2 under regeneration gas

The selective catalytic reduction of NO over Ce0.3TiOx-supported metal oxide catalysts

[Selective Catalytic Reduction of NO on Ag, Co and Cu/Al2O3 in Excess Oxygen].