Abstract:A series of vanadium based catalysts (VxMn(4-x)Mo3Ce3/Ti) with different vanadium (x wt.%) and manganese ((4-x) wt.%) contents have been prepared by the wet impregnation method and investigated for selective catalytic reduction (SCR) of NOx by NH3 in the presence of 8 vol.% H2O and 500 ppmV SO2. The physicochemical characteristics of the catalysts were thoroughly characterized. The SCR of NOx by NH3 (NH3-SCR) activity, especially the low-temperature activity, significantly increased with increasing V2O5 content in the catalyst until the V2O5 content reached 1.5 wt.%, which corresponds well with the redox properties of the catalyst. All of the metal oxides were well dispersed and strongly interacted with each other on the catalyst surface. V mainly exists in the V5+ state in the catalysts. The strong synergistic effect between the vanadium and cerium species led to formation of more Ce3+ species, and that between the vanadium and manganese species contributed to formation of more manganese species with low valences. All of the catalysts exhibited strong acidity, while the redox properties determined the NH3-SCR activity, especially the low-temperature activity. H2O and SO2 had severe inhibiting effects on the activity of V1.5Mn2.5Mo3Ce3/Ti. However, good H2O and SO2 resistance and high NOx conversion by V1.5Mn2.5Mo3Ce3/Ti could be achieved in the presence of SO2 and almost no decline was observed in a long-term test at 275°C for 168 hr in the presence of SO2 and H2O, which can be attributed to the sulfate species formed on the catalyst surface.

Catalytic Reduction of NO with NH 3 over V 2 O 5 -MnO X /TiO 2 -Carbon Nanotube Composites

Promotional Effects of Carbon Nanotubes on V2O5/TiO2 for NOX Removal.

Selective catalytic reduction of NOX with ammonia over Mn–Ce–OX/TiO2-carbon nanotube composites

Catalytic Reduction of Nox over Mnox Coated Tio2 Nanotube Arrays

VxMn(4-x)Mo3Ce3/Ti catalysts for selective catalytic reduction of NO by NH3

Highly dispersed V2O5/TiO2 modified with transition metals (Cu, Fe, Mn, Co) as efficient catalysts for the selective reduction of NO with NH3

Low temperature selective catalytic reduction of NOx by NH3 over Cu modified V2O5/TiO2–carbon nanotube catalyst

Performance of V_2O_5-WO_3-MoO_3/TiO_2 Catalyst for Selective Catalytic Reduction of NO_x by NH_3

Catalytic Reduction of NOx with NH3 over Different-Shaped MnO2 at Low Temperature

In Situ Supported Mnox-Ceox On Carbon Nanotubes For The Low-Temperature Selective Catalytic Reduction Of No With Nh3

Experimental Study on Preparation of V_2O_5-WO_3-MoO_3/TiO_2 Catalysts and Selective Reduction of NO_x with NH_3

Carbon nanomaterial-SmMn2O5 nanocrystal composites with highly efficient catalytic oxidation of NO

Investigations of Surface VOx Species and Their Contributions to Activities of VOx/Ti0.5Sn0.5O2 Catalysts Toward Selective Catalytic Reduction of NO by NH3

Promotional effect of CeOX for NO reduction over V2O5/TiO2-carbon nanotube composites

Enhanced Catalytic Performance of V2O5–WO3/Fe2O3/TiO2microspheres for Selective Catalytic Reduction of NO by NH3

MnOx-CeOx/CNTs pyridine-thermally prepared via a novel in situ deposition strategy for selective catalytic reduction of NO with NH3

Low Temperature Selective Catalytic Reduction of NO over Manganese Supported on TiO2 Nanotubes

Selective catalytic reduction of NO with NH3 over CuOX-carbonaceous materials

Bifunctional catalysts V-Cu/TiO 2 for selective catalytic reduction of NO x and CO oxidation under oxygen-rich conditions

Catalytic Reduction of NO by NH3 over Fe–Cu–OX/CNTs-TiO2 Composites at Low Temperature

Nh3 Selective Catalytic Reduction of No: A Large Surface Tio2 Support and Its Promotion of V2o5 Dispersion on the Prepared Catalyst