Low Temperature Selective Catalytic Reduction of NO over Manganese Supported on TiO2 Nanotubes
Yao YAO,Shu-le ZHANG,Qin ZHONG,Xiao-xiao LIU
DOI: https://doi.org/10.1016/s1872-5813(11)60042-x
2011-01-01
Abstract:Titanate nanotubes were synthesized hydrothermally from commercial TiO2 nanoparticles in the presence of NaOH; after calcination at 400°C, TiO2 nanotubes were obtained, which were used as the support to prepare manganese catalyst (MnOx/TiNT) by wet impregnation for the low-temperature selective catalytic reduction (SCR) of NO. The results of Brunauer, Emmett and Teller study, transmission electron microscopy, X-ray diffraction, and thermogravimetric measurements showed that TiO2 nanotubes exist in a well-defined TiO2 anatase phase after calcination at 400°C and that manganese particles are highly dispersed on the wall of TiO2 nanotubes. The effects of active-component loading, space velocity, oxygen content, [NH3]/[NO] ratio, and NO concentration on the SCR performance of MnOx/TiNT were investigated in a simulated flue gas. Under the reaction conditions of 150°C, [NH3]/[NO] of 1.2, [O2] of 3%, [NO] of 0.06%, gas hour space velocity of 23613.8 h−1, and Mn loading of 5–15%, NO conversion exceeds 95%. The catalyst is deactivated in the presence of H2O at 180°C, but its activity can be recovered almost completely by cutting off H2O. Moreover, higher resistance to H2O is observed at higher temperatures. The presence of SO2 can also deactivate the catalyst gradually; however, the catalyst shows better resistance to SO2 in the presence of H2O than in its absence. The SCR activity of the MnOx/TiNT catalyst that is deactivated by SO2 increases gradually after cutting off H2O and SO2 but cannot be restored to its initial level.